Abstract:A fine-grained TiAl alloy with composition of Ti-45Al-5.5(Cr,Nb,B,Ta)(mole fraction,%) was prepared by double mechanical milling(DMM) and spark plasma sintering(SPS).The effects of sintering temperature on the microstructure and mechanical properties of the Ti-45Al-5.5(Cr,Nb,B,Ta) were studied by X-ray diffractometry(XRD), scanning electron microscopy(SEM) and mechanical testing machine.The results show that the morphology of double mechanical milling powder is regular with sizes of 10-40μm and the internal structure is even.TiAl and Ti_3Al are the main phases in the powders,with few phases such as Ti_3Al,Ti_2Al and TiB_2 observed in the SPS bulk samples of Ti-45Al-5.5(Cr,Nb,B,Ta) alloy.For samples sintered at 1 000℃,the microstructure of equiaxed crystal grain with sizes less than 500 nm is achieved.For samples sintered at 1 100℃,the sizes of few equiaxed crystal grain obviously increases.The SPS bulk samples exhibit better microstructures.The micro-hardness of the SPS bulk samples at 1 000℃is obviously lower than that of the SPS bulk samples at 1 100℃.The compression strength and bending strength of the SPS bulk samples at 1 000℃is obviously higher than that of the SPS bulk samples at 1 100℃.On the base of analysis of fractographies,it shows that the compression fracture transformation of the SPS Ti-45Al-5.5(Cr,Nb,B,Ta) alloy at 1 000℃is intergranular rupture and that at 1 100℃is intergranular rupture and cleavage fracture.The bending fracture transformation of the SPS Ti-45Al-5.5(Cr,Nb,B,Ta) alloy samples is intergranular rupture and cleavage fracture.

Microstructure of TiAl alloy prepared by intense plastic deformation and subsequent reaction sintering

Microstructure and Properties of A Tial Alloy Prepared by Mechanical Milling and Subsequent Reactive Sintering

Microstructures and Mechanical Properties of TiAl Alloy Prepared by Spark Plasma Sintering

Preparation of TiAl-based alloys by mechanical milling and reactive sintering

Microstructure and Mechanical Properties of Tial-Based Alloy Prepared by Double Mechanical Milling and Spark Plasma Sintering

Synthesis of Tial Based Alloy by Mechanical Milling, Warm Pressing and Reactive Sintering

Microstructural Characters of TiAl Intermetallics Prepared with Different Processes

Effect of Microstructure on the Hot Deformation Behavior of TiAl-Based Alloys Prepared by Powder Metallurgy Method

Drastic enhancement in hot-workability and microstructural refinement of TiAl alloys via martensitic transformation: A comparative study

Manufacturing a TiAl Alloy by High-Energy Ball Milling and Subsequent Reactive Sintering

Preparation of Ti-45Al-5.5(Cr,Nb,B,Ta) Alloy by Mechanical Milling and Spark Plasma Sintering

Preparation of fine-grains TiAl alloys by mechanical alloying and spark plasma sintering

Investigation on the Influence of Mechanical Milling on Microstructure and Thermostability of Ti/Al Mixed Powders

Microstructure and mechanical properties of Ti-43Al-9V alloy fabricated by spark plasma sintering

Fine-grained TiAl alloy prepared by double mechanical milling and spark plasma sintering

Investigation on microstructure and properties of Ti-45Al-5.5(Cr, Nb, B, Ta) alloy prepared by double mechanical milling (DMM) and spark plasma

Synthesis and Properties of an Ultrafine Grained Ti-45al-2cr-2nb-1b-0.5ta Alloy Prepared by Double Mechanical Milling and Spark Plasma Sintering

Effect of mechanical milling on diffusive reaction of Ti-Al composite powders

Microstructural Evolution and Mechanical Properties of a High Yttrium Containing TiAl Based Alloy Densified by Spark Plasma Sintering

Effects of Sintering Temperature on Microstructure Evolution and Hot Deformation Behavior of TiAl-Based Alloys Prepared by Spark Plasma Sintering

Microstructure evolution and tensile property of TiAl alloy using continuous direct energy deposition technique