Abstract:To improve the oxidation resistances of SiC coated C/C composites by a pack cementation (PC) method at high temperature and alleviate the siliconization erosion of molten silicon on C/C substrate during the preparation of SiC coating, a SiO2-SiC reticulated layer with SiC nanowires was pre-prepared on C/C composites through combined slurry painting and thermal treatment before the fabrication of SiC coating. The presence of porous SiO2-SiC layer with SiC nanowires was beneficial to fabricate a compact and homogeneous SiC coating resulting from synergistic effect of further reaction between SiO2 and pack powders and the reinforcement of SiC nanowires. Therefore, the results of thermal shock and isothermal oxidation tests showed that the mass loss of modified SiC coating was only 0.02 % after suffering 50-time thermal cycles between room temperature and 1773 K and decreased from 5.95 % to 1.08 % after static oxidation for 49.5 h in air at 1773 K. Moreover, due to the blocking effect of SiO2-SiC reticulated layer on siliconization erosion during PC, the flexural strength of SiC coated C/C composites with SiO2-SiC reticulated layer increased by 64.8 % compared with the untreated specimen.

Preparation, properties and protection mechanism for oxidation resistant coatings of Cf/SiC composites

Microstructure and oxidation behavior of SiOC coatings on C/C composites co-deposited with HMDS and TEOS by using CVD process

A ZrB2–SiC/SiC Oxidation Protective Dual-Layer Coating for Carbon/carbon Composites

Oxidation Protection of C/C Composites with a Multilayer Coating of SiC and Si + SiC + SiC Nanowires

A Multilayer MoSi2–SiC–B Coating to Protect SiC-coated Carbon/carbon Composites Against Oxidation

Preparation of a multi-composition coating for oxidation protection of modified carbon-bonded carbon fiber composites by a rapid sintering method

Microstructure and Oxidation Resistant Property of C/C Composites Modified by SiC–MoSi2–CrSi2 Coating

A gradient composite coating to protect SiC-coated C/C composites against oxidation at mid and high temperature for long-life service

Microstructure And Oxidation Resistance Of Carbon/Carbon Composites Coated With Si3n4-Si/Mosi2-Sic Multi-Layers By Slurry Coating And Post Heat-Treatment Process

In-situ SiC nanowires reinforced SiC-based multicomponent ceramic coating for protecting SiOC/CF composites

A dense ZrB2-SiC-Si/SiC-Si coating to protect carbon/carbon composites against oxidation at 1773 K and 1973 K

A Thick SiC-Si Coating Prepared by One-Step Pack Cementation for Long-Term Protection of Carbon/carbon Composites Against Oxidation at 1773 K

ZrB2 particles reinforced glass coating for oxidation protection of carbon/carbon composites

Oxidation Protection of C/C Composites by Ultra Long SiC Nanowire-Reinforced SiC–Si Coating

ZrB2–SiC Gradient Oxidation Protective Coating for Carbon/carbon Composites

SiC Nanowire-Toughened SiC–MoSi2–CrSi2 Oxidation Protective Coating for Carbon/carbon Composites

Oxidation Protection Of Zrb2-Sic Modified Carbon-Bonded Carbon Fiber Composites

Oxidation Protection and Behavior of In-Situ Zirconium Diboride–silicon Carbide Coating for Carbon/carbon Composites

Preparation and oxidation behavious of SiO2 and SiC coating 3-D braided carbon fiber

Interfacial modification and oxidation resistance behavior of a CVD-SiC coating for C/SiC composites

Improved antioxidative and mechanical properties of SiC coated C/C composites via a SiO2-SiC reticulated layer