Abstract:Stress corrosion cracking (SCC) is one of the main ageing mechanism in light water reactor (LWR). 316L austenitic stainless steel was adopted in nuclear industry for its relatively high corrosion resistance. The SCC of austenitic stainless steel may occur as it is subjected to both the tensile stress and the caustic medium, with regard to maintaining the structural integrity of components in nuclear power plant, an accurate prediction and efficient assessment of the component lifetime is significant and necessary. The stress corrosion crack propagation behavior of the 316L stainless steel elbow of nuclear power plant was investigated through a numerical simulation method. Firstly a finite element (FE) model was created for the stainless steel thick-walled elbow (the outer diameter is 355.6 mm, the inner diameter is 275.6 mm), with a semi-elliptical shaped 3D defect introduced at the internal surface of the elbow as the geometry of the crack, which was consistent with a practical crack, the crack opening displacement (delta(i)) was determined by the calculations through the Dugdale model; subsequently, according to the FE calculation results, establish the fitting formula of the stress intensity factor (K) varying with the crack depth (a) and additional stress (P), and the fitting formula of the stress corrosion crack propagation rate (da/dt) for elbows under two types of cold work deformation was deduced through the combination with the experimental data, the crack propagation time was then calculated using a iterative method for cracks which evolved from different initial crack depth values to certain crack depth values. The calculation results provided effective reference criterion for the nuclear power plant safety assesment. This investigation demonstrated that, when the cold deformation extent of the elbow part is relatively small (with the hardness of 230 similar to 245 HV) and it is under the ideal condition (no initial additional stress), it takes around 57 a for the stress corrosion crack to penetrate the elbow, when the initial additional stress was elevated to 200 MPa, the elbow failure time was shrinked to 1/5 (no stress release), 2/7 (half-stress release) and 3/7 (total stress release) of the former; keep the same initial additional stress (200 MPa) and increase the cold work deformation extent (the hardness was increased from 230 similar to 245 HV to 275 similar to 300 HV), the elbow failure time was shortened to 2/5 (no stress release), 3/8 (half-stress release) and 1/3 (total stress release) for the elbow part with higher cold deformation extent compared to the part with lower cold deformation extent, thus it was observed that both the decrease of the extent of stress relaxation and the increase of the extent of cold work deformation contributed to the reduction of the residual life of the nuclear power plant 316L stainless steel elbow.

Analysis of Failure in Elbow of Radiation Superheater of 500 MW Boiler in a Power Plant

Cause analysis of elbow crack for header's connecting tubes of boiler's reheater concerning 300 mw unit

Failure analysis of reheater tubes in a 350 MW supercritical circulating fluidized bed boiler

Study on Stress Intensity of Welding Parts of Small Dlameter Tube to Reheater in Coal-burning Thermo-electric Factory with 200 MW Power

Failure Analysis on Unexpected Fracture of the Hydraulic Expansion Mandrel for Tube to Tubesheet Expanding in the Steam Generator of Nuclear Power Plant

Failture Analysis of Welded Joint on Superheater of a 670t/h Boiler

Root Cause Analysis for Cracked Pipe in Auxiliary System in Nuclear Power Plant

Failure Analysis on Abnormal Bursting of Heat Transfer Tubes in Spiral-Wound Heat Exchanger for Nuclear Power Plant

Study on failure mechanism of suspension lug elbow in an ethylene cracking pyrolyzer

Safety Testing and Analysis of the Header of the Drawn Boiler with a Small Diameter and a Large Wall Thickness

Remaining Life of Superheater Elbow Tube by Finite Element Method

Analysis on the cause of crack in connection pipeline of subcritical boiler reheater

Analysis of Frequent Tube Burst of High Temperature Reheater in 600 MW Unit

Failure Analysis on Abnormal Thinning of Elbows in the Economizer at Waste Heat Boiler System

Cause Analysis of Superheater Tube Cracking in Medium Temperature Separated Circulating Fluidized Bed Boiler

Failure Analysis of an Elbow Tube Break in a Pyrolysis Furnace

Creep-fatigue Endurance of a Superheater Tube Plate under Non-Isothermal Loading and Multi-Dwell Condition

Analysis on reason of tube cracking of platen superheater during commissioning of supercritical boiler

Failure Analysis of T91 Finish Superheater Tube in 660 MW Supercritical Thermal Power Plant

Failure behavior analysis of oxide film formed on super-heater tubes of boiler during deep peak process

Life Prediction for Stress Corrosion Behavior of 316l Stainless Steel Elbow of Nuclear Power Plant