Abstract:A series of Ni-SiO2 aerogel and xerogel catalysts were prepared by sol-gel supercritical drying (SCD) and general drying methods using tetraethylorthosilicate (TEOS) as a precursor of silica and nickel nitrate as starting material of nickel. Water or alcohol was used as solvent. Based on the experimental results of nitrogen adsorption-desorption, XRD, temperature-programmed reduction (TPR), IR, temperature-programmed desorption of hydrogen (H-2-TPD) and activity evaluation, the physical and chemical properties and catalytic performance of the catalysts for hydrogenation of m-dinitrobenzene to m-phenylenediamine were investigated. Both the Ni-SiO2 aerogel catalysts had high specific surface areas, but their catalytic activity and selectivity were low due to their small active surface areas caused by sintering of nickel crystallite. For the Ni-SiO2 xerogel catalyst that used alcohol as solvent, well-dispersed nickel particles were formed, but the strong interaction between nickel and the support made the catalyst difficult to be reduced, thus resulting in lower degree of the utilization of metal. However, the xerogel catalyst that made use of water solution exhibited the highest catalytic activity and selectivity for m-phenylenediamine attributed to its higher surface area of active nickel, over which the conversion of m-dinitrobenzene and the yield of m-phenylenediamine were up to 92.6% and 88.4%, respectively, under the conditions of 2.6 MPa and 373 K after reaction for 1 h.

Roles Of Tio2 Nanoparticles In The Formation Of Monolithic Silica Gels Via Bulk Sol-Gel Process

Sol-Gel Preparation, Characterization and Hydrogenation Property of Silica Supported Ni Catalyst

Preparation of TiO2 nanoparticles on the surface of SiO2 in binary liquids

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Preparation of Nanometer Tio2/Sio2 Composite Materials by Adsorption Phase Nanoreactor Technique

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

TiO2–Ag Nanocomposites by Low‐Temperature Sol–Gel Processing

Sol–gel Synthesis of Macroporous TiO 2 from Ionic Precursors Via Phase Separation Route

Fabrication of the Monolithic Materials Via Novel Monocomponent Sol-Gel Process

pH control on preparation of nano-TiO_2 by gel-sol process

From nano aggregates to nano plates: The roles of gelatin in the crystallization of titanium silicate-1

Silica–Titania mixed Oxides: Si–O–Ti Connectivity, Coordination of Titanium, and Surface Acidic Properties

Preparation and Properties of Nanostructure Anatase Tio2 Monoliths Using 1-Butyl-3-methylimidazolium Tetrafluoroborate Room-Temperature Ionic Liquids As Template Solvents

A novel bulk sol-gel process to prepare monolithic silica materials

Macroporous Sio2 Monoliths Prepared Via Sol-Gel Process Accompanied by Phase Separation

Preparation and Characterization of Hierarchically Porous Monolithic TiO2

Sol–Gel Preparation and Electrorheological Activity of SiO2–TiO2Composite Powders

Effect of Inorganic Ions on Gelation, Particle Morphology, and Texture of Solo-Gel-Derived Silica Nanospheres

Synthesis of Mesoporous Tetragonal ZrO2, TiO2 and Solid Solutions and Effect of Colloidal Silica on Porosity

Fabrication of Nanogel Core–silica Shell and Hollow Silica Nanoparticles Via an Interfacial Sol–gel Process Triggered by Transition-Metal Salt in Inverse Systems