Abstract:In this paper, a novel nanoporous barium titanate (BaTiO3) crystalline powder was synthesized by using triblock poly(ethylene oxide) (PEO) and poly(propylene oxide) (PPO) based systems (P-123) as the soft template via a sol-gel method and their structure-dependent electro rheological property was studied. The pore diameter and specific surface area of BaTiO3 were precisely controlled by varing the calcined temperature. The chemical composition, structure and surface morphology of BaTiO3 were characterized by X-ray diffraction (XRD), thermo gravimetric analysis (TGA), and nitrogen adsorption-desorption method, scanning electron microscopy (SEM) and transmission electron microscopy (TEM). The result revealed that the pore volume and specific surface area of BaTiO3 decreased with the increment of calcined temperature. The electro rheological fluids (ERFs) were obtained by dispersing BaTiO3 crystallites in silicon oil and three kinds ERFs were fabricated by using three kinds of BaTiO3 which were prepared under different calcined temperature (550, 600 and 900 A degrees C) as the precursors. The behaviors of the ERFs were evaluated via a rotational rheometer fixed with electric field generator. The results showed that electro rheological effect was related to the pore volume and specific surface area of BaTiO3. Due to the distinct advantage of sol-gel method for preparing nanoporous BaTiO3 without contamination of the materials, the markedly low current destiny of the ERFs was obtained. The yield stress of ERFs with large specific surface area of BaTiO3 reached the maximum of 3 kPa, which is higher than that of ERFs using traditional pure BaTiO3 crystallites (lower than 1 kPa).

Sol–Gel Preparation and Electrorheological Activity of SiO2–TiO2Composite Powders

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

Structure and Electrorheological Properties of Nanoporous BaTiO3 Crystalline Powders Prepared by Sol–gel Method

The Effects of Substrate on the Properties of Sol-Gel Derived TiO2 Films

Investigation on the Microstructure and Optical Performance of TiO_2 Films by Sol-Gel Method

Synthesis of porous silica gel and study on the adsorption of cerium

Investigation of the Tetraethoxysilane‐derived Sol–gel Process by Rheological Oscillation Test and the Effect of Different Synthetic Parameters

Preparation of Modified Electrorheological Fluid and Property Testing

Preparation of Macroporous and Mesoporous Tio2 Film with Various Solvents

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Mechanism investigation of influence of HPC on the microstructure of TiO2 films

ELECTRORHEOLOGICAL BEHAVIOR OF THE SUSPENSIONS OF SURFACTANT COATED TiO2

Effects of HPC on the Microstructure and Hydrophilicity of Sol–gel-Derived TiO2 Films

Synthesis of silica bearing sulfobetaine and sulfonic groups and their electrorheological response

Room-Temperature Preparation of TiO2-SiO2 Composite Film and Its Properties

Effect of Incorporation of Silver on the Electrical Properties of Sol-Gel-Derived Titania Film

Electrorheological fluids containing Ce-doped titania

Preparation and Electrorheological Properties of Peanut‐Like Hollow Core–Shell Structure TiO2@SiO2 Nanoparticles

Influence of water contents on structure and properties of SiO 2-PEDT composite antistatic thin film by sol-gel process

Sol-gel process kinetics for Si(OEt)4

Characterization and Electrical Properties of Sol-Gel Synthesized (sr, Pb)TiO3 Powders