Abstract:For development of thin bioactive coatings on metal implants, a dense and uniform apatite layer was coated onto titanium (Ti) implants in situ by using a new biomimetic method, which is composed of apatite nucleation and growth steps in simulated body fluid (SBF). Analysis of the coatings by thin film X-ray diffraction and scanning electron microscopy-energy dispersive X-ray microanalysis (SEM-EMPA) before implantation showed that its characteristics were very similar to those of natural bone. The coated and uncoated rectangular plates were bilaterally implanted into the tibial proximal metaphyses of rabbits. After 6, 10 and 25 weeks post-implantation, the bone bonding and bone formation at the bone-implant interfaces were evaluated by a detachment test and undecalcified histological examination. Mechanical testing in tension showed that the failure load of apatite layer-coated Ti implants was significantly higher than that of uncoated control at each time period (all P < 0.001). Histologically, it was shown that bone was deposited directly onto the apatite coating without any intervening soft tissue, while in the paired controls, interpositional soft tissue was seen at the bone-implant interface. By SEM-EPMA, a uniform calcium- and phosphorus-rich layer was detected between the coated implants and bone, but not in uncoated controls at either earlier or later time periods. The results indicate that the apatite layer deposited on Ti in situ may significantly increase the bone bonding strength by providing a bioactive surface, which allows for an early bone apposition to the implant. In addition, the apatite layer-coated Ti produced by the biomimetic process may fulfil the requirements of favourable thin coatings and strong adhesion at the metal-coating interface.

Formation of apatite on porous titanium in different supersaturated calcification solution

Effect of Supersaturation on the Morphology of Hydroxyapatite Crystals Deposited by Electrochemical Deposition on Titanium

Apatite deposition on thermally and anodically oxidized titanium surfaces in a simulated body fluid.

[Experimental Study of Fast Formation of Biomimetic Apatite Coatings on Pure Titanium Surface].

A Comparative Study of in Vitro Apatite Deposition on Heat-, H2O2-, and NaOH-treated Titanium Surfaces

Biomimetic Deposition of Apatite on Electrochemically Oxidized Titanium Substrates

Morphologies of Hydroxyapatite Crystal Deposited on Titanium Surface with Electrochemical Technique

[Fast Formation of Biomimetic Apatite Coatings on Pure Porous Titanium Implant's Surface].

Synthesis and Charaterization of Silicon-Substituted Hydroxyapatite Coating by Electrochemical Deposition on Ti Substrate

Evolution of the magnesium incorporated amorphous calcium phosphate to nano-crystallized hydroxyapatite in alkaline solution

Carbonate apatite coating on titanium induced rapidly by precalcification.

Longer-Term Mechanical And Biological Evaluation Of Titanium Alloy Coated With Apatite Layer

Ribbon-like and rod-like hydroxyapatite crystals deposited on titanium surface with electrochemical method

Apatite Layer-Coated Titanium for Use As Bone Bonding Implants

Mechanism of apatite formation on pure titanium treated with alkaline solution

Influence of Solution Conditions on Deposition of Calcium Phosphate on Titanium by NaOH-treatment

Controlled crystal growth of calcium phosphate on titanium surface by NaOH-treatment

In vitro apatite formation on nano-crystalline titania layer aligned parallel to Ti6Al4V alloy substrates with sub-millimeter gap

Formation and characteristics of the apatite layer on plasma-sprayed hydroxyapatite coatings in simulated body fluid

Bioactive Composite Coating on Titanium Implants for Hard Tissue Repair

Apatite Formation on Rutile and Anatase Layers Derived by Hydrolysis of Titanylsulfate in a Simulated Body Fluid