Abstract:Fused silica crucibles are commonly used in the fabrication process of solar grade silicon ingots. These crucibles are manufactured from high purity natural quartz sand and as a consequence, their properties are influenced by the presence of water and hydroxyls in the raw quartz. In this work, diffuse reflectance IR, 1H magic angle spinning NMR, and Raman spectroscopy were used to investigate the influence of thermal treatment on water and hydroxyl groups in high purity natural quartz sand. Most of the water in dry sand is present in the form of closed inclusions within the quartz grains which were detected in Raman imaging studies, even after thermally treating the samples at 600 °C. Only after heating to 900 °C did this water completely vanish, most likely as a result of rupturing of the inclusions. However, newly formed OH groups, identified as isolated and hydrogen bound OH were observed as products of the reaction between water and quartz. Similarly, liquid water was observed in NMR spectra even after treatment at 600 °C while at temperatures >900 °C, only non-interacting silanol groups were present. The comparison of the temperature dependence of the IR and NMR spectra also yields insight into the assignment of the OH stretching mode region of the IR spectrum in this system. The intensity of water related bands decreases while the intensity of OH bands first increases and then decreases with increasing temperature. The band intensity of Al-rich defects as well as the characteristic feature at 3200 cm-1 does not follow the temperature dependence of typical water peaks. It is also shown that leaching the quartz sand in HF solution helps to remove water from inclusions, likely by forming pathways for fluid flow inside the quartz grains. Milling of the samples caused formation of an additional type of hydroxyl group, possibly due to partial amorphisation of the surfaces of the quartz grains surface during the process. The results improve the basis for a knowledge-based processes development for the processing of high purity natural quartz.

The study of preparing "low-water" content quartz glass by sol-gel method

Sol–gel preparation of Ge nanocrystals embedded in SiO2 glasses

Rapid-quenching of High-Pressure Depolymerized Hydrous Silicate (peridotitic) Glasses

A Study of Formation and Photoluminescence Properties of ZnO Quantum Dot Doped Zinc-Alumino-silicate Glass Ceramic

Preparation and characterization of ZnO-B2O3-SO2 by sol-gel method

Preparation and Characterization of ZnO-B2O3-SiO2 by Sol-Gel Method

Study of Eu3+-doped Luminescence Glasses Prepared by a Sol-Gel Process

Preparation of multilayer coated glass with low-E and thermal insulation properties

Preparation of Zirconia Powders by Sol-gel Process

Study on Preparation of Silica Sol by Silicon Dissolution & Dripping water glass Method

Sol-gel Preparation of a Silica Antireflective Coating with Enhanced Hydrophobicity and Optical Stability in Vacuum

Structural evolution of water and hydroxyl groups during thermal, mechanical and chemical treatment of high purity natural quartz

Study on CdS/SiO2 Quantum-dot-glass Prepared by Sol-gel Method

Realizing Translucency in Aluminosilicate Glass at Ultralow Temperature Via Cold Sintering Process

Fabrication of SiO2 and SiO2-ZrO2 gel glasses by non-hydrolytic sol-gel process

Obtaining transparent silica glass from nano-silica hydrosol

The preparation of silica-based SiO2-ZrO2 films as waveguides by sol-gel process

Improvement of Fluorescence Lifetime from Er-Doped Sol-Gel Silica Glass by Dehydration in CCl4

LOW-TEMPERATURE SYNTHESIS OF ZRO2-TIO2-SIO2 GLASSES FROM ZR(NO3)4.5H2O, SI(OC2H5)4 AND TI(OC4H9)4 BY THE SOL-GEL METHOD

Mgo-Al2o3-Sio2 Glass-Ceramic Prepared by Sol-Gel Method

Ultra-low temperature preparation of mullite glass-ceramics with high transparency sintered from EMT-type zeolite