Abstract:The high temperature compressive tests of squeeze casting ZK60 magnesium alloy in the testing temperature range of 523-723K and strain rate range of 0.001-10s-1 were performed on Gleeble-1500D thermal simulator testing machine. Optical microscopy was performed to elaborate on the dynamic recrystallization (DRX) grain growth. TEM observation indicated that the mechanical twinning, dislocation slip, and dynamic recrystallization are the materials typical deformation features. Variations of flow behavior with deformation temperature as well as strain rate were analyzed. Analysis of the flowing deformation behavior and microstructure observations indicated that the flow localization was observed at lower testing temperature and higher strain rates. Dynamic recrystallization occurred at higher testing temperature and moderate strain rates, which improved the ductility of the material. The results indicated that at the testing temperatures lower than 573K and strain rates higher than 1s-1, the material exhibited flow instability manifesting as bands of flow localizations. These temperatures and strain rates should be avoided in processing the material. Dynamic recrystallization occurs in the temperature range 573-723K and the strain rate range 0.001-0.1s-1. The number of dynamic recrystallization grains is less at lower temperature and higher strain rate than higher temperature and lower strain rate. The dynamic recrystallization is inadequate at 573-623K while the dynamic recrystallization grain growth has been observed in the temperature range of 673-723K. Therefore it may be considered that the optimum processing parameters for hot working of squeeze casting ZK60 magnesium alloy are 648K and 0.001-0.01s-1, at which fine dynamic recrystallization microstructure can be obtained.

Dynamic Recrystallization of AZ91 Magnesium Alloy During Compression Deformation at Elevated Temperature

Dynamic Recrystallization and Microstructure Evolution in AZ31 Magnesium Alloy During Thermomechanical Processing

Deformation Behaviour and Dynamic Recrystallization of AZ61 Magnesium Alloy

High Temperature Compressive Deformation Behaviors of Extruded Az91 Magnesium Alloy

Compressive Deformation of ZK60 Magnesium Alloy at Elevated Temperature

Hot Deformation Behavior of AZ91 Magnesium Alloy in Temperature Ranging from 350°C to 425°C

Dynamic Recrystallization Behavior of Az61 Magnesium Alloy

Microstructure in as-cast AZ61 magnesium alloy during hot compression deformation

Microstructure Evolution of AZ91D Magnesium Alloy During High Temperature Compression

Deformation Behavior of ZK60 Magnesium Alloy at Elevated Temperature

Microstructural Evolution of Az61 Magnesium Alloy During Hot Deformation

Influence of Strain Rate on Dynamic Recrystallization Behavior and Hot Formability of Basal-Textured AZ80 Magnesium Alloy

Effect of Strain Rate on Dynamic Recrystallization in a Magnesium Alloy under Compression at High Temperature

Dynamic Recrystallization Kinetics of As-Cast AZ91D Alloy

Dynamic Recrystallization Mechanisms During Hot Compression of Mg–Gd–Y–Nd–Zr Alloy

Dynamic Recrystallization Behavior and Hot Workability of Mg–2.0Zn–0.3Zr–0.9Y Alloy by Using Hot Compression Test

Hot deformation behavior of as-Cast AZ61 magnesium alloy

Continuous Dynamic Recrystallization and Deformation Behavior of an AA1050 Aluminum Alloy during High-Temperature Compression

Hot compression behavior of AZ91 alloy(III) - Recrystallization kinetics based on cellular automata simulation

Deformation Behavior and Dynamic Recrystallization of a Mg–Zn–Y–Zr Alloy

Hot Deformation Behavior and Microstructural Evolution of Twin-Roll-Casting Mg Alloy during High-Temperature Compression