Dynamic Recrystallization Mechanisms During Hot Compression of Mg–Gd–Y–Nd–Zr Alloy

Yi-ping Wu,Xin-ming Zhang,Yun-lai Deng,Chang-ping Tang,Liu Yang,Ying-ying Zhong
DOI: https://doi.org/10.1016/s1003-6326(15)63789-x
2015-01-01
Abstract:Hot compression tests were conducted on a homogenized Mg–7Gd–4Y–1Nd–0.5Zr alloy at 450 °C and a strain rate of 2 s−1. Dynamic recrystallization (DRX) mechanisms were investigated by optical microscope (OM), scanning electron microscope (SEM) and transmission electron microscope (TEM) systematically. The crystallographic orientation information is obtained through electron back-scattering diffraction (EBSD). The result shows that the flow stress firstly reaches a peak rapidly followed by declining to a valley, and then increases gradually again when the alloy is compressed to a strain of −1.88. DRX related to {10 2} tensile twins is extensively observed at small strains, resulting in an evident grain refinement. DRX grains first nucleate along the edges of twin boundaries with about 30° 〈0001〉 off the twin parents. While at large strains, conventional continuous DRX (CDRX) is frequently identified by the formation of small DRX grains along the original grain boundaries and the continuously increasing misorientation from the centre of large original grains to the grain boundaries. Evidence of particle-stimulated nucleation (PSN) is also observed in the present alloy.
What problem does this paper attempt to address?