Abstract:This study investigated the dynamic recrystallization (DRX) mechanism and hot-deformation behavior of the solution-treated Mg-0.5Bi-0.5Sn-0.5Mn (BTM000) alloy during hot compression at temperatures ranging from 175 to 225 °C with a strain rate of 0.001–1 s −1 . Processing maps and constitutive equation were used for a detailed analysis. The results showed a strong correlation with a coefficient of 0.987669, indicating the accuracy of proposed method in predicting the hot deformation behavior. The average activation energy ( Q ) was found to be 139.10 kJ/mol, and the stress component ( n) was calculated to be 7.96, suggesting that cross-slip is the primary deformation mechanism. Based on the processing maps, the most suitable processing conditions were found to be within the range of 210–290 °C with a strain rate of 0.37–1 s −1 . At a low strain rate of 0.001 s −1 , the dominant deformation mechanism observed was pyramidal slip. However, at higher temperatures (175–325 °C) and a strain rate of 1 s −1 , a transformation from basal slip to a combination of basal slip and pyramidal slip was observed. Under low-temperature and low-strain-rate conditions (175 °C/0.001 s −1 ), continuous dynamic recrystallization (CDRX) was the dominant mechanism. In contrast, under other deformation conditions (175 °C/1 s −1 , 325 °C/0.001 s −1 , 325 °C/1 s −1 ), a synergistic effect between discontinuous dynamic recrystallization (DDRX) and CDRX was evident. Through quasi-situ kernel average misorientation (KAM) characterization, it was observed that the local storage energy associated with CDRX was significantly lower compared to the combination of CDRX and DDRX, indicating a higher likelihood of CDRX occurrence.

Investigation of hot deformation behavior of Mg-14Gd-0.5Zr (wt%) through constitutive analysis and processing maps

Hot Deformation and Processing Map of As-Homogenized Mg–9Gd–3Y–2Zn–0.5Zr Alloy

Hot Deformation Behavior and Processing Map of Coarse-Grained Mg–Gd–Y–Nd–Zr Alloy

Hot compression behavior and microstructure evolution of Mg-Gd-Y-Zn-Zr alloy

Hot compression behavior, simulation verification and dynamic recrystallization mechanism of Mg-Gd-Y-Zr alloy

Thermal Deformation Behavior and Processing Maps of As-Homogenized Mg-5.8 Zn-0.5 Zr-1.0 Yb Alloy

Characterization of Hot Deformation Behavior and Processing Maps of Homogenized Al-Mg-Si-Sc-Zr Alloys

Construction of Dynamic Recrystallization Critical Strain Model, Kinetic Model, and Hot Workability of Mg–8Gd–4Sm–1Zn–0.5Zr Alloy

Hot Deformation Behaviour and Constitutive Equation of Mg-9Gd-4Y-2Zn-0.5Zr Alloy

Deformation-induced Dynamic Precipitation of 14H-LPSO Structure and Its Effect on Dynamic Recrystallization in Hot-Extruded Mg-Y-Zn Alloys

Study on Thermal Compression Deformation Behavior and Constitutive Model of Homogenized Mg–5Zn–1Mn Alloy

Investigations on Microstructure and Mechanical Properties of Cast Mg-Gd-Y-Zn-Zr-Nd Alloy

Deformation Behavior and Dynamic Recrystallization of Mg-Y-Nd-Gd-Zr Alloy

Hot deformation behavior and resultant microstructural evolution of dilute Mg–Bi–Sn–Mn alloy during hot compression

Effect of strain rate on dynamic recrystallization mechanism of Mg-Gd-Y-Sm-Zr alloy during hot compression

A comprehensive analysis on microstructure evolution of Mg-5.65Zn-0.66Zr alloy during hot deformation

Hot Deformation Behavior and Finite Element Simulation of Mg–8.3Gd–4.4Y–1.5Zn–0.8Mn Alloy

Deformation Behavior and Dynamic Recrystallization of a Mg–Zn–Y–Zr Alloy

High strain rate compression deformation mechanism and constitutive equation of fine grained Mg–7Gd–5Y–1.2Nd–0.5Zr alloy at different temperatures

Mechanical Behavior and Microstructure Evolution of Mg-Gd-Y-Zn-Zr Alloy during Multipass Hot Compression Deformation

Effect of Deformation Parameters on Recrystallization Behavior and Long-Period Stacking-Ordered Phase of Mg-9Gd-4Y-2Zn-0.5Zr Alloy