Dynamic Recrystallization Behavior of Az61 Magnesium Alloy

HT Zhou,AQ Yan,CM Liu
IF: 3.752
2005-01-01
Transactions of Nonferrous Metals Society of China
Abstract:An AZ61 alloy was subjected to hot compression at temperatures ranging from 523 K to 673 K, with strain rates of 0.001 - 1 s(-1). Flow softening occurs at all temperatures and strain rates. There are peak and plateau stresses on flow curves. The initiation and evolution of dynamic recrystallization(DRX) were studied by the flow softening mechanism based on the flow curves and microstructural observations. A linear relationship was established between the logarithmic value of the critical strain for DRX initiation(ln(epsilon c),) and the logarithmic value of the Zener-Hollomon parameter (InZ). The volume fraction of DRX grain (phi a) is formulated as a function of the process parameters including strain rate, temperature, and strain. The calculated values of phi a agree well with the values extracted from the flow curves. The size of DRX grain(d) was also formulated as a function of the Zener-Hollomon parameter. This study suggests that DRX behavior of AZ61 can be predicated from plastic process parameters.
What problem does this paper attempt to address?