Wear mechanism of electrodeposited amorphous Ni-Fe-P alloys

Chenghui Gao,Yuan Zhao,高诚辉,赵源

IF: 3.752

2004-01-01

Transactions of Nonferrous Metals Society of China

Abstract:The wear mechanism of amorphous Ni-Fe-P coating was discussed. The wear resistance of the amorphous Ni-Fe-P coatings was tested on a Timken wear apparatus, and the wear track of the amorphous Ni-Fe-P coatings as-deposited and heated at various temperatures was observed by SEM. The results show that the wear resistance reaches a maximum value at NaHPO2 (.) H2O concentration of 5 g/L, and heating at 400 degreesC. The wear mode of The coating will change with the heating temperature increasing from pitting + plowing at 200 degreesC to pitting at 400 degreesC, and to plowing at 600 degreesC. The pits on the worn surface of the amorphous Ni-Fe-P coating result from the tribo-fatigue fracture. The cracks of spalling initiate at pits and propagate at certain angle with the sliding direction on surface, and then extend into sub-surface along the poor P layers or the interface between layers. Finally under repeated action of the stress in the rubbing process the cracks meet and the debris forms. The generation of the pits and spalling is related with the internal stress, brittleness and layer structure of the amorphous Ni-Fe-P coating.