Preparation, Microstructure and Friction properties of Cold Sprayed Fe-based Amorphous Composite Coating

Li Xu,Wang Qiang,Mao Xuan,Niu Wenjuan,Wang Lu,Li Nan,Han Pen

2021-01-01

Rare Metal Materials and Engineering

Abstract:Fe87.4Cr2.5Si6.8B2.4C0.9 amorphous alloy powder was pretreated by the liquid nitrogen-room temperature cyclic cryogenic treatment method and the amorphous coating was prepared on the 6061 aluminum alloy substrate surface by adjusting the technological parameters of cold spraying. The influence mechanism of cryogenic treatment on the deposition behavior of amorphous powder and the microstructure of coating were studied. The frictional wear property of the amorphous coating was investigated by friction-wear test. The results show that the thickness of coating prepared by original amorphous powder is only 6 mu m, and the amorphous particles are discontinuously distributed on the surface of the substrate. Only the amorphous particles with smaller particle size can have effective plastic deformation, but the crystallization rate is low during the deposition of the powder. The average thickness of the coating prepared by cryogenic treated amorphous powder is 67 mu m, and the amorphous alloy particles in the coating are uniformly distributed. The amorphous particles with larger particle size can also undergo effective plastic deformation, but the crystallization rate is higher during the powder deposition. The main wear mechanism of 6061 aluminum alloy substrate in the process of friction and wear is adhesive wear and fatigue wear, and the main wear mechanism of amorphous coating is abrasive wear. The wear mass loss of the amorphous coating prepared by the original amorphous powder and the cyclic cryogenic treated powder is 15.7% and 11.8% of that of the 6061 aluminum alloy substrate, respectively.