Bonding Mechanism and Fracture Behavior of Cold-Sprayed Fe-based Amorphous Alloy on 6061 Al Alloy

Peng Han,Qiang Wang,Wenjuan Niu,Shukai Ge,Mingfan Wan,Nan Li,Runling Qian
DOI: https://doi.org/10.1016/j.surfcoat.2024.131194
IF: 4.865
2024-01-01
Surface and Coatings Technology
Abstract:Using cold spray technology to prepare amorphous alloy coatings can effectively prevent crystallization, thereby preserving the excellent properties of amorphous alloys. However, interfacial bonding significantly affects performance, such as weak bonding impacting the durability and stability of the coating. Therefore, in-depth study of the interfacial bonding mechanism is crucial for a comprehensive understanding of coating properties. This paper uses cold spray technology to prepare Fe-based amorphous alloy coating on 6061 aluminum alloy substrates. The bonding mechanisms at the particle/substrate, particle/particle, and coating/substrate interfaces are studied, and the fracture behavior in the tensile bond strength test is analyzed. The results show that the heat accumulation and the increase in strain rate generated by the particles impacting the substrate cause the viscosity of the amorphous alloy to suddenly decrease from 1.2 x 103 3 g & sdot;cm- & sdot; cm- 1 s- 1 to 8.4 x 10-- 1 g & sdot;cm- 1 & sdot; cm- 1 s- 1 . Increased fluidity and micro-friction accelerate the mixing of elements and form a metallurgical bond at the particle/ substrate interface. Meanwhile, the oxides at the particle/particle interface are extruded, and the exposed fresh metal is subjected to a huge shear rate to promote atomic fusion. Tamping of the subsequent particles leads to further deformation of the deposited particles, forming a stronger metallurgical bond and mechanical anchoring at the particle/particle interface. In addition, the continuous impact of particles triggers dynamic recrystallization of the substrate, and the average grain size decreases from 14.28 mu m to 1.39 mu m. This fine-grained structure strengthens the mechanical anchoring of the coating/substrate interface. Furthermore, the bonding strength measured by the tensile test is determined to be 18.51 MPa. The main reasons for the final fracture occurring in the coating are the coating pores, cracks formed by shear bands accumulated in free volume, and the low adhesion oxide layer at the particle interface.
What problem does this paper attempt to address?