Abstract:Aluminum coatings can provide galvanic cathodic protection for several metals and alloys. In order to be a suitable protective solution on structural components, the mechanical integrity must be preserved. In particular, the fatigue properties are a challenge for thermal spray protective coatings on mechanical structures. To address the issue of the fatigue integrity of 7075 aluminum alloy with an arc sprayed protective coating, different surface preparations prior to arc spraying were considered. In the present work, a feasibility study was performed using laser ablation as a surface preparation technique before or during arc spraying of coatings through collaboration between the LERMPS laboratory in France, the National Research Council of Canada and the Royal Military College of Canada. Both fatigue and adhesive properties of aluminum coatings were evaluated in relation to substrate surface preparation techniques including laser ablation (PROTAL® process), grit blasting and shot peening. Results indicate that a combination of key conditions including using nitrogen as the arc spray gas, shot peening and proper laser energy density for ablation provides high fatigue resistance of metallic coated 7075 alloy substrates. Specimens prepared under these conditions show a similar fatigue resistance to uncoated substrates. Les revêtements en aluminium peuvent fournir une protection galvanique cathodique à plusieurs métaux et alliages. Afin de constituer une solution protectrice adéquate pour les éléments de structure, le procédé d’application du revètement doit préserver l’intégrité mécanique du substrat. En particulier, les propriétés de fatigue constituent un défi pour les revêtements protecteurs par projection thermique sur les structures mécaniques. Pour examiner le problème de l’intégrité de la fatigue de l’alliage d’aluminium 7075 avec un revêtement protecteur appliqué par projection à l’arc électrique, on a considéré différentes préparations de la surface avant l’application. Dans le travail présent, on a effectué une étude de faisabilité en utilisant l’ablation laser comme technique de préparation de la surface avant ou pendant l’application à l’arc de revêtements, par l’intermédiaire d’une collaboration entre le laboratoire LERMPS en France, le Conseil National de la Recherche du Canada et le Collège Militaire Royal du Canada. On a évalué les propriétés de fatigue ainsi que de résistance d’adhérence de revêtements en aluminium, en relation avec les techniques de préparation de la surface du substrat, incluant l’ablation laser (procédé PROTAL®), le sablage au jet de sable et le grenaillage. Les résultats indiquent qu’une combinaison de conditions clés incluant l’usage de l’azote comme gaz de projection à l’arc, le grenaillage et une densité appropriée d’énergie du laser pour l’ablation fourni une résistance élevée à la fatigue de substrats d’alliage 7075 revêtus d’un revètement métallique . Les échantillons préparés sous ces conditions montrent une résistance à la fatigue similaire aux substrats non revêtus.

Effect of substrate surface finish and particle velocity on fatigue performance of cold spray coated A6061 aluminum alloy

Effects of post-deposition processing on static and cyclic performance of cold sprayed 6061 aluminum alloy

Laser Assisted Cold Spray of Aluminum Alloy 6061: Experimental Results

Bonding Mechanism and Fracture Behavior of Cold-Sprayed Fe-based Amorphous Alloy on 6061 Al Alloy

Effect of Grit Blasting and Subsequent Cold Spraying on Low-Cycle Fatigue Crack Growth of Q355B Steel

Mechanical Properties and Growth Mechanisms of Long and Small Fatigue Cracks in As-deposited Bulk Cold Spray Al-6061

Mechanical Performance of Cold-Sprayed A357 Aluminum Alloy Coatings for Repair and Additive Manufacturing

Effect of the substrate surface and coating powder hardness on the formation of a cold sprayed composite layer

Recover the Tensile Strength of Hard Aluminum Alloy Through Laser Assisted Cold Spray

Effects of Laser Shock Peening on Interfacial Bonding Strength of Cold-Sprayed Coating

Study on effects of heat treatment on morphology of Al coating on the surface of Mg alloy by cold spray

Microstructural and interfacial characteristics of supersonic reclaimed 2024Al-T3 substrate using cold sprayed 2024Al deposit

Wear and Corrosion Properties of 316L-SiC Composite Coating Deposited by Cold Spray on Magnesium Alloy

Comparison of Cold-Sprayed Coatings of Copper-Based Composite Deposited on AZ31B Magnesium Alloy and 6061 T6 Aluminum Alloy Substrates

Enhanced Electrochemical and Tribological Properties of AZ91D Magnesium Alloy via Cold Spraying of Aluminum Alloy

Influence of Al2O3 content on microstructure, electrical conductivity and adhesion strength of cold sprayed Al-Al2O3 coatings on PEEK substrate

Effect of Cold-Spray Parameters on Surface Roughness, Thickness and Adhesion of Copper-Based Composite Coating on Aluminum Alloy 6061 T6 Substrate

Effect of Substrate Surface Roughness on Microstructure and Mechanical Properties of Cold-Sprayed Ti6Al4V Coatings on Ti6Al4V Substrates

Influence of spray angle in cold spray deposition of Ti-6Al-4V coatings on Al6061-T6 substrates

ALUMINUM PROTECTIVE COATINGS - FATIGUE AND BOND STRENGTH PROPERTIES WITH RESPECT TO SURFACE PREPARATION TECHNIQUES: LASER ABLATION, SHOT PEENING AND GRIT BLASTING

Bonding mechanisms in cold spray deposition of gas atomised and solution heat-treated Al 6061 powder by EBSD