Abstract:The severe oxidation of metal elements leads to a large amount of oxide inclusions that hinder the formation of metallurgical bonds across intersplat interfaces during thermal spraying in an ambient atmosphere, which further degrades the performance of thermally sprayed metal coatings. Controlling the oxidation of metal elements during spray deposition remains a significant challenge. In this paper, the thermodynamic and kinetic requirements of in-situ in-flight deoxidation by adding deoxidizer elements (diamond particles) to Fe / Al spray powders to achieve oxide-free molten droplets in an ambient atmosphere were investigated. Fe / Al / 2.5C composite powders containing 2.5wt.% diamond particles were prepared by mechanical alloying. Atmospheric plasma spraying (APS) was used to generate an oxide-free molten spray of FeAl particles at temperatures higher than 2 000 degrees C. This was achieved by the in-situ self-oxide cleaning effect of in-flight particles by carbon, which prevented metal droplets from oxidizing in an open atmosphere. For comparison, a FeAl coating was also deposited using Fe / Al composite powders prepared by mechanical alloying. The particle velocity and temperature were measured by a commercial thermal-spraying particle diagnostic system. The microstructures of the coatings were characterized by scanning electron microscopy and X-ray diffraction. The chemical compositions of the coatings were measured by inductively coupled plasma spectroscopy. The adhesive strength and hardness of the plasma-sprayed FeAl-based coatings were tested. The results show that under the combined effects of plasma- jet heating and the FeAl exothermic reaction, the heated FeAl spray particles could reach a high temperature of over 2 100 degrees C, which meets the thermodynamic conditions for carbon in-situ deoxidation. Because oxidation occurs from the surface of an in-flight molten droplet, to maintain continuous deoxidation of the molten FeAl droplet, the rapid transfer of carbon from the interior of the molten droplet to the surface is necessary. It was confirmed that the strong convection flow of the molten metal droplets satisfied the kinetic conditions of carbon in-situ in-flight deoxidation. The oxygen content in the APS-sprayed FeAl coatings increased with the increase of the spray distance. In contrast, the oxygen content in the APS-sprayed FeAl / 2.5C coatings decreased from 1.01 wt.% to 0.48 wt.% as the spray distance increased from 70 mm to 150 mm. This was accompanied by the decrease in carbon content from 1.41 wt.% to 0.31 wt.%, indicating the effective protection of Fe and Al from oxidation by the carbon in the droplet. Compared with the oxygen content of 3.67 wt.% in traditional FeAl coating, the oxygen content of the FeAl / 2.5C coatings was reduced to less than 0.5 wt.%. Considering that the carbon content of the coatings decreased as the spray distance increased, the results confirm that the in-flight oxidation of Fe and Al was suppressed by the preferential sacrificial oxidation of carbon in the molten droplets. Thus, the oxide in the FeAl / 2.5C coatings was mainly attributed to post-deposition oxidation. Moreover, the FeAl droplet reached the temperature to realize the spread-fusing self-metallurgical bonding effect for FeAl splats. The coatings exhibited a dense microstructure with an apparent porosity of less than 0.5%. The adhesive bonding strength of the prepared coatings exceeded 59.2 MPa owing to metallurgical bonding. The hardness of the coatings reached 590 HV0. 3, which was approximately twice that of traditional FeAl coatings. This was attributed to the reinforcement provided by the Fe3AlCx cementite phase resulting from the residual carbon in the coating.

Improving the adhesion of cold sprayed Al deposits through in-situ micro-forging

Remarkable improvement in microstructure and mechanical properties of cold sprayed Al deposits via impact forging post-spray treatment

The Mechanisms of Enhancement of Inter-Particle Bonding in In-Situ Micro-Forging Assisted Cold Spray

Improving Corrosion Resistance of Al6061 Coating Deposited by an In-Situ Shot-Peening Assisted Cold Spray

Solid-state Additive Manufacturing High Performance Aluminum Alloy 6061 Enabled by an In-Situ Micro-Forging Assisted Cold Spray

Improving Adhesion Strength and Electrical Conductivity of Cold-Sprayed Al Deposit on Cu Substrate Through Friction-Stir-Processing

Microstructure and Properties Tailoring of Cold Sprayed Metals

Bonding Mechanism and Fracture Behavior of Cold-Sprayed Fe-based Amorphous Alloy on 6061 Al Alloy

Deposition Behavior, Microstructure and Mechanical Properties of an In-Situ Micro-Forging Assisted Cold Spray Enabled Additively Manufactured Inconel 718 Alloy

Study on Impact Fusion at Particle Interfaces and Its Effect on Coating Microstructure in Cold Spraying

Nanocrystallization of interfacial microstructure of deformed particles in cold sprayed Ti6Al4V deposits

Tuning the microstructure and mechanical properties of additive manufactured aluminum matrix composites by cold spray

Study of Aluminum Bronze Coating by Cold Spray Process

Microstructural Characterization of Cold-Sprayed Nanostructured FeAl Intermetallic Compound Coating and Its Ball-Milled Feedstock Powders

Optimization of In-Situ Shot-Peening-Assisted Cold Spraying Parameters for Full Corrosion Protection of Mg Alloy by Fully Dense Al-Based Alloy Coating

Improvement of the deposition efficiency and adhesion strength of cold sprayed fluoropolymer coating by laser surface texturing of the substrate

Formation of Fe-Al Intermetallic Compound Coating Through Cold Spraying

Influence of Al2O3 content on microstructure, electrical conductivity and adhesion strength of cold sprayed Al-Al2O3 coatings on PEEK substrate

Effect of Cold Spray Processes on Friction Stir Welded Microstructures of AZ31 Magnesium Alloys

Microstructural and interfacial characteristics of supersonic reclaimed 2024Al-T3 substrate using cold sprayed 2024Al deposit

Mechanism of Suppressing Oxidation of FeAl Molten Droplet by Adding C to Powder and Its Effect on Microstructure and Properties of Plasma-sprayed Coating