Abstract:Electroless nickel composite coatings have the potential for high-temperature tribological applications, and a combination of high wear resistance and low friction factor is one of the desirable solutions but still a tricky problem. The addition of self-lubricating WS2 and hard Si3N4 nanoparticles to the Ni-P coatings is expected to obtain good high-temperature tribological performance. In this work, Ni-P-Si3N4-WS2 composite coatings with various contents of WS2 nanoparticles were prepared using electroless plating and subsequently annealed at 400 °C in an inert atmosphere. The tribological properties of the coatings were evaluated using a ball-on-disc wear instrument at operating temperatures from 25 to 600 °C. The microstructure, chemical composition, and surface morphology of the coatings were characterized by X-ray diffractometry (XRD), energy disperse spectroscopy (EDS), and scanning electron microscopy (SEM). Upon increasing the WS2 dosage in the bath, the WS2 content in the coating increased and the micro-hardness of the as-plated coating increased from 539 to 717 HV. After heat treatment, the coating underwent a crystallization process, and the hardness increased from 878 to 1094 HV. The main wear mechanism of the coating changed from adhesive wear in the as-plated state to abrasive wear in the annealed state. The annealed Ni-P-Si3N4-WS2 coating with a WS2 dosage of 2.5 g/L in the bath exhibited excellent mechanical properties, with a hardness of 10.9 GPa, a friction coefficient of ~0.51, and a wear rate of 8.4 × 10−15 m3N−1×m−1 at room temperature, and maintained optimal performance at high temperatures. At operating temperatures of 200, 400, and 600 °C, the form of wear was adhesive wear for coatings with a WS2 dosage < 1.5 g/L and abrasive wear for coatings with a WS2 dosage ≥ 1.5 g/L. The synergism of WS2 and Si3N4 particles refined the grains of the Ni-P matrix in as-plated coatings and obviously reduced the friction coefficient of friction pairs in annealed coatings at all operating temperatures.

Preparation and Properties of Ni–Co–P/nano‐sized Si3N4 Electroless Composite Coatings

Fabrication and performance of Ni-Co-P/Si3N4 electroplated composite coatings on al-si alloys

Fabrication and Performance of Ni-Co-P/Si<sub>3</sub>N<sub>4</sub> Electroplated Composite Coatings on Al-Si Alloys

Enhanced Mechanical and Tribological Capabilities of a Silicon Aluminum Alloy with an Electroplated Ni–Co–P/Si3N4 Composite Coating

High Temperature Tribological Behavior of Electroless Plating Ni-P-Si3N4-WS2 Composite Coatings

Electroless Ni-P-Sic Composite Coatings with Superfine Particles

Preparation and Tribological Properties of the Carbon Nanotubes–ni–p Composite Coating

Study of fabrication and wear properties of Ni–SiC composite coatings on A356 aluminum alloy

Study on Preparation and Properties of Nano Ni-SiC Amorphous Composite Coatings

Microstructure and mechanical properties of electroless Ni–P–Si 3 N 4 –TiN composite coatings

Ni-Co-P/Si_3N_4 Electroless Composite Plating and Its Hardness

Microstructure of Nanometer-sized Al2O3 Composite Coating Prepared by Electroless Plating

Synthesis and Tribological Behavior of Electroless Ni–P–WC Nanocomposite Coatings

Preparation of Ni-Cnt Composite Coatings on Aluminum Substrate and Its Friction and Wear Behavior

Friction and wear behaviors of electrodeposited Ni-P-CNTs composite coatings on Al-alloy substrate

Friction and Wear of Electroless Ni-P-CS Composite Coating

Effects of Cobalt Content on Mechanical and Corrosion Properties of Electroless Ni‐Co‐P/TiN Nanocomposite Coatings

Influence of Ni-addition on Mechanical, Tribological Properties and Oxidation Resistance of AlCrSiN Coatings

Sediment Co-Deposition of Nanostructured Ni-Al2o3 Composite Coatings

Deposition Mechanism and Wear Resistance Nano Ni-Al2O3 Composite Coatings

Influence of Electrodeposition Process Parameters and Si3N4 Nanoparticle Concentration on Microhardness and Wettability of Ni-Co-Si3N4 Nanocomposite Coatings