Influence of Carbon Matrix on the Tribology of C/C Composites Used As Shaft Sealing Ring

葛毅成,易茂中

DOI: https://doi.org/10.3321/j.issn:1000-6893.2004.06.021

2004-01-01

Abstract:On M2000 wear machine, coupled with 40Cr steel, four kinds of C/C composites with different carbon matrix structures have been tested under different loadings for friction and wear characteristics. The results show: the RL(rough layer) structure sample gets the highest friction coefficient 0.151～0.165 and fluctuating with loading increase;and the SL(smooth layer) structure sample gets the lowest friction coefficient 0.105～0.118 and decreasing slowly with loading increase. With time prolonging, the friction coefficient of RL structure sample decreases under high loading, while that of SL structure sample increases a little except under 60N. Under all the loadings, the friction coefficient of resin carbon densified sample decreases with time prolonging, but that of SL+resin carbon structure sample shows the variety trend being different under different loadings. The bulk wear loss of RL structure sample is the highest which could reach 1.61 mm~3 under 150N, and that of SL+resin carbon structure sample is the least. The SEM observations show: with loading increase, the wear surface of RL sample changs only a little, while that of the resin carbon sample exhibits more and more severe surface fiber drawn phenomenon, and the SL+resin carbon structure sample exhibits more and more smooth wear surface.