Abstract:Two kinds of C/C composites with rough-lamination pyrocarbon matrix (RL) or smooth lamination (SL) pyrocarbon matrix were prepared. The sliding friction behaviors against 40Cr steel ring of the two C/C composites, a high strength graphite and a pyrocarbon solid material with SL structure used as compared material were investigated. The wear surface of the samples were observed by SEM. The results show that the PAN-carbon fiber can improve the frictional stability of C/C composites. Compared with the graphite, the coefficients of friction (COF) of the RL-C/C are lower under the same load of about 0.08?0.12, and the increasing range of the volume losses are still lower than those of the graphite. Compared with the SL pyrocarbon material, the COF and the volume loss of the SL-C/C are about 0.02?0.05 and 0.2 mm3, lower than those under the same load. The COFs of most RL-C/C and SL-C/C specimens remain stable or decrease slightly with time, while those of the graphite and pyrocarbon specimens increase. The thickness of the integrated friction film of the RL-C/C decreases with load, but the wear surface of the SL-C/C is rough. Tough the wear surface of the graphite is integrated, the serious abrasive wear make the debris move easily and accumulate on the edge of the wear trace to form a restacked morphology. On the wear surface of the pyrocarbon material, some loosed debris, circular worn holes and flake worn out pyrocarbon has been found.

Comparative Study on the Friction and Wear Behaviors of C/C Composites and High-Strength Graphite at Elevated Temperature

A Comparative Investigation of the Tribological Behavior and Wear Mechanism of Bronze-graphite Composite under Dry- and Water-lubricated Sliding Against Steel

Sliding Friction Wear Behaviors of C/C Composites Coupled with GH4169 Alloy and High-Strength Graphite

TRIBOLOGY PROPERTIES OF C/C COMPOSITES AND GRAPHITE AT NON-LUBRICATION WEAR ENVIRONMENT

The Effect of C/C Composites Characteristic on Sliding Friction and Wear Behavior

Friction and Wear Behavior of Carbon Material and C/C Composites with Similar Structure

Sliding Friction and Wear Behavior of C/C Composites Against 40 Cr Steel

Dry Wear Behaviors of Graphite/cermet Self-Lubricating Composite under Different Sliding Conditions and Simulation of Temperature Field

Study on friction and wear behaviors of ceramic-graphite composite

Wear behavior of C/C-Cu composites under different loads and couple parts

Friction and wear properties of C/C-Cu composites sliding at various velocities

To-fro sliding tribological behavior of C/C composite under different loads

Friction and Wear Behaviors of B4c/6061al Composite

Influence of Carbon Matrix on the Tribology of C/C Composites Used As Shaft Sealing Ring

Friction and Wear Behavior of Copper-Graphite Composite Material in High-Speed Sliding with Current

Influence of Oxidation on the High-Temperature Tribological Properties of Tungsten-Carbide-Reinforced Cu-Ni-Mn Composite Coatings

Comparative Investigation on the Fretting and Sliding Wear Properties of TC4 Against GCr15 under Different Temperatures

Effects of Graphite Contents on the Microstructure Evolution, Mechanical Properties and High Temperature Tribological Behavior of Cu–Ni–Al/Gr Solid-Lubricating Composites

Sliding Friction and Wear Behavior of C/C Composite Ring Against C/C Composite Block

Testing and Analysis of Frictional Performance of Carbon Fiber/Metal Composite Materials

Study on friction performance of carbon/carbon composite under lubrication condition