Study on the Relationship Between the Properties of Copper-graphite Composite and the Shape and Particle Size of Graphite
Rushi CHEN,Zhu XIAO,Jie DAI,Zhou LI,Guofu XU
DOI: https://doi.org/10.13258/j.cnki.nmme.2019.05.001
2019-01-01
Abstract:Using electrolytic copper powder, flake graphite and near spherical graphite powder with different particle sizes as raw materials, the copper graphite composite was prepared by vacuum hot pressing sintering process. The effects of graphite shape and size on the microstructure, density, relative density, electrical conductivity, hardness and compression strength were investigated. The wear behavior of the composite was evaluated by using a pin-on-disc friction and wear tester. The effects of graphite shape and particle size on the friction and wear properties of the composite were studied by analyzing the morphology of the wear surface. The results show that, comparing to flaky graphite powder, the use of near spherical graphite powder with the same particle size is beneficial to improve the density of the composite and obtain more excellent mechanical properties with the compressive strength increased by nearly 65 MPa. With particle size of near spherical graphite decreased from 19 μm to 4 μm, the density, conductivity, hardness, compressive strength and friction coefficient of the composite are decreased gradually, while the wear amount is increased gradually. The conductivity of the composite is decreased from 28.6 %IACS to 20.6 %IACS, and the compressive strength is decreased by nearly 30 MPa.