Abstract:Carbon fiber-reinforced polymers (CFRPs) are being used extensively in modern industries that require a high strength-to-weight ratio, such as aerospace, automotive, motorsport, and sports equipment. However, although reinforcement with carbon fibers improves the mechanical properties of polymers, this comes at the expense of abrasive wear resistance. Therefore, to efficiently utilize CFRPs in dry sliding contacts, solid lubricant is used as a filler. Further, to facilitate the fabrication of objects with complex geometries, selective laser sintering (SLS) can be employed. Accordingly, in the present work, graphite-filled carbon fiber-reinforced polyamide 12 (CFR-PA12) specimens were prepared using the SLS process to explore the dry sliding friction and wear characteristics of the composite. The test specimens were aligned along four different orientations in the build chamber of the SLS machine to determine the orientation-dependent tribological properties. The experiments were conducted using a pin-on-disc tribometer to measure the coefficient of friction (COF), interface temperature, friction-induced noise, and specific wear rate. In addition, scanning electron microscopy (SEM) of tribo-surfaces was conducted to specify the dominant wear pattern. The results indicated that the steady-state COF, contact temperature, and wear pattern of graphite-filled CFR-PA12 are orientation-independent and that the contact temperature is likely to approach an asymptote far below the glass transition temperature of amorphous PA12 zones, thus eliminating the possibility of matrix softening. Additionally, the results showed that the Z-oriented specimen exhibits the lowest level of friction-induced noise along with the highest wear resistance. Moreover, SEM of tribo-surfaces determined that abrasive wear is the dominant wear pattern.

Tribological Behavior of Phenolic Resin-Based Friction Composites Filled with Graphite

Tribological behavior of modified polyetheretherketone composites in sliding against stainless steel under water lubrication

A Comparative Investigation of the Tribological Behavior and Wear Mechanism of Bronze-graphite Composite under Dry- and Water-lubricated Sliding Against Steel

Influence of the Addition of Nano-porous Graphite/Parafffin Additive on the Wear Properties of Phenol-Formaldehyde Resin Composites

Tribological Properties of Carbon Fabric/Epoxy Composites Filled with FGr@MoS2 Hybrids under Dry Sliding Conditions

Investigation of Tribological Behavior of Polytetrafluoroethylene/graphene Composite

Tribological Behavior of Poly(tetrafluoroethylene) and Its Composites Reinforced by Carbon Nanotubes and Graphene Sheets: Molecular Dynamics Simulation

Effect of lubricant functional groups on tribological properties of epoxy/graphene composites

Tribological Characteristics of a Friction Composition of Metal-Ceramic Powders and Carbon-Containing Additives on a Polymer Binder

Tribological behaviors of Ag−graphite composites reinforced with spherical graphite

On the tribological behaviors of Cu matrix composites with different Cu-coated graphite content

Dry Friction and Wear Behavior of Laser-Sintered Graphite/Carbon Fiber/Polyamide 12 Composite

Mechanochemical functionality of graphene additives in ultralow wear polytetrafluoroethylene composites

Tribological Behavior of Carbon-Nanotube-Filled PTFE Composites

Study on the lubrication film formation and characteristics of different graphite seal composites

Friction and Wear Behaviour of AA2024/ZrO2 Composites: Effect of Graphite

Tribological investigation into nickel-coated graphite polytetrafluoroethylene composites

Tribological Properties of EP Composites Reinforced with Short Glass Fiber, Graphite, PTFE and B4C Under Oil Lubrication

Tribological Properties of Surface-Modified Graphene Filled Carbon Fabric/Polyimide Composites

Investigation of the way to enhance the synergistic effect between polyimide and graphene on the tribological performance of polytetrafluoroethylene composites

Tribological properties of reaction-formed graphite/SiC composites under water-lubricated conditions