Tribological behaviors of Ag−graphite composites reinforced with spherical graphite

SUN Yang,WANG Yan,LI Yun,Ke-chao ZHOU,Lei ZHANG,Yang SUN,Yan WANG,Yun LI
DOI: https://doi.org/10.1016/s1003-6326(20)65370-5
IF: 3.752
2020-08-01
Transactions of Nonferrous Metals Society of China
Abstract:Two kinds of Ag−graphite composites reinforced with spherical graphite (SG) and conventional flake graphite (FG) were prepared by powder metallurgy technology. The effect of graphite morphology on the tribological behavior for the Ag−SG and Ag−FG under the dry sliding wear was investigated with a pin-on-disk tribometer at a load of 3.0 N in atmosphere condition. The results indicated that the minimum wear rate of 3.5×10<sup>−5</sup> mm<sup>3</sup>/(N·m) for Ag−FG was achieved and it reduced by nearly an order of magnitude, reaching 1.6×10<sup>−6</sup> mm<sup>3</sup>/(N·m) for the Ag−SG. The obviously different tribological behaviors between the Ag−SG and Ag−FG were closely related to the formation of cracks in the sub-surface. The stress concentration tended to generate at the edges of flake graphite during sliding process, which resulted in the cracks and severe delamination wear of Ag−FG. However, no cracks were found around the spherical graphite in Ag−SG. The spherical graphite can effectively inhibit the initiation and propagation of cracks, achieving high wear resistance.
metallurgy & metallurgical engineering
What problem does this paper attempt to address?
The paper aims to study the tribological behavior of silver-based composites reinforced with different forms of graphite (spherical graphite SG and traditional flake graphite FG) under dry sliding wear conditions. Specifically, the researchers prepared two types of silver-graphite composites using powder metallurgy technology and conducted friction and wear tests using a pin-on-disk tribometer under atmospheric conditions with a load of 3.0 Newtons. The study found that compared to the traditional flake graphite-reinforced silver-based composite (Ag−FG), the spherical graphite-reinforced silver-based composite (Ag−SG) exhibited significantly lower wear rates, reducing from 3.5×10^−5 mm³/(N·m) to 1.6×10^−6 mm³/(N·m), nearly an order of magnitude decrease. This significant difference in tribological behavior is closely related to the formation of subsurface cracks in the material. During sliding, stress concentration easily occurs at the edges of the flake graphite, leading to cracks and severe delamination wear in the Ag−FG composite. However, in the Ag−SG composite, no cracks were observed around the spherical graphite. The spherical graphite can effectively inhibit the initiation and propagation of cracks, thereby achieving higher wear resistance. Therefore, the focus of this study is to explore the impact of graphite morphology on the tribological performance of silver-based self-lubricating composites, with the aim of achieving better tribological performance and longer service life.