Influence of Fiber Orientation on Sliding Tribology Behavior of C/C Composite

Yi-cheng GE,Mao-zhong YI,Li-ya LI

DOI: https://doi.org/10.3321/j.issn:1004-0595.2006.06.011

2006-01-01

Abstract:Influence of fiber direction of C/C composite on the sliding tribology behavior was studied using M-2000 wear tester at room temperature without lubrication. With the increase in load, the changing extent of friction coefficient of the samples with the fibers axis parallel to the sliding orientation (X) was lower than that of the samples with the fiber axis perpendicular to the sliding direction or worn surface (Y or Z samples). The debris on worn surface of the samples with X direction was more easily to be moved and the wear volume loss was larger than those of the samples with Y and Z direction. The moving ability of the debris on the worn surface of the samples with Y and Z direction was low and was easily to form friction film, but the fibers on the worn surface of such samples were more easily to be cut under high test load. For the samples with smooth lamination structure pyrocarbon matrix, the wear volume losses of the samples with X direction changed from 0.426-0.997 mm3 with the increase in test loads, those of the samples with Y direction were 0.448-1.020 mm3, while those of the samples with Z direction were 0.349-1.420 mm3; for the samples with resin carbon matrix, the wear volume losses of the samples with X direction were 0.429-1.134 mm3 while those of the samples with Y direction were 0.237-0.981 mm3.