Sliding Friction Behavior of C/C Composites with Water Lubrication Using 40Cr Coated by Cr Ring

Ge Yicheng,Yi Maozhong,Li Liya

DOI: https://doi.org/10.3969/j.issn.0254-0150.2007.03.004

2007-01-01

Abstract:The friction and wear behavior of three kinds of C/C composites(C/C) with different matrix carbon was tested with water lubrication using M2000 wear tester.The results show that with the increase in load,the friction coefficient of the three C/C increases at first and then decreases.The friction coefficient of composite A densified by chemical vapor infiltration (CVI) has the highest changed extent among the three composites that is among 0.04～0.09,but those of composite B densified by resin impregnation(RI) or composite C densified by CVI+RI only change among 0.05～0.063.The wear volume loss of the three C/C increases with the increase in load,composite C has the lowest wear volume loss that is among 1.7～4.5 mm3.With the increase in time,the friction coefficients of all samples remain stable.The SEM images show that the worn surface of all samples becomes more and more integrated with the increase in load.On the worn surface of composite B,the resin carbon near the fiber has the ring shape worn morphology;the pyrocarbon debris of composite C has the sheet shape worn morphology.The fiber with the axis perpendicular to the sliding direction has the helical crack morphology.