Abstract:With the 40Cr steel couple coated by Cr, the sliding tribology behavior of two kinds of C/C composites with different matrix was tested using a M2000 wear tester. The results show that with the increasing of load, the friction coefficients of the composite with resin carbon matrix(RC) decrease quickly from 0.156 under 60 N to 0.123 under 150 N, while those of the composite with rough lamination/smooth lamination /resin carbon (RL/SL/RC) change only between 0.122 and 0.101. The wear volume loss of the two composites increases except for under 100 N. The SEM morphology shows that with the increasing of load, the worn surface of the composite with RC becomes more and more integrated while the size of the debris becomes less and less. The Raman spectrum shows that the graphitization on the worn surface of the fibers draws down after 100 N, the graphitization of the boundary between the fiber and the matrix carbon rises up to 150 N, but the graphitization of the matrix carbon draws down all the while. With the increasing of load, the graphitization on the worn surface of all the worn areas becomes closer and closer, which indicates the worn surface of the different component has the similar friction ability. The composites with RL/SL/RC have better tribological characteristic than the composite with RC.

Wear behavior of C/C-Cu composites under different loads and couple parts

Tribological behavior of C/C-Cu composites

Friction and wear properties of C/C-Cu composites sliding at various velocities

Comparative study of friction and wear behavior of C/C/Cu and C/Cu composites

Electrical Sliding Wear Behavior of C/C-Cu Composites

Study of Friction and Wear Properties of Cu/Short Carbon Fibers Composites

Influence of Applied Load on Wear Behavior of C/C-Cu Composites under Electric Current

Tribological characteristic of C/C-Cu composites under variable testing mode

Effect of C/C preform on the triboiogical behavior of C/C-Cu composites

Effect of copper coated graphite powder content on the microstructure and properties of Cu/C composite

Tribological Behavior of a Novel C/C-Cu Sliding Electrical Contact Material

Effects of Speed and Load on Loading Wear and Friction Resistance of Al2O3/Cu Composites

A Study on the Friction and Wear Properties of Ceramic-Enhanced Cu-Based Composites

Tribological Behavior of Cu Matrix Composites Containing Graphite and Tungsten Disulfide

Influence of Load on Sliding Tribology of C/C Composite with 40cr Steel Couple Coated by Cr

Friction and wear properties of copper matrix composites reinforced with short carbon fibers

Sliding Friction and Wear Behavior of C/C Composites Against 40 Cr Steel

Sliding Friction Behavior of C/C Composites with Water Lubrication Using 40Cr Coated by Cr Ring

Microstructure and Tribological Properties of Cu Modified C/C- SiC Composites

Fretting wear behavior of brass/copper-graphite composites as a contactor material under electrical contact