Microstructure of Ceramic Coatings Formed on Ti-6Al-4V Alloy by Microarc Oxidation in NaAlO2 Solution
Wen-bin Xue,Zhi-wei Deng,Yong-liang Li,Ru-yi Chen,Tong-he Zhang
DOI: https://doi.org/10.3969/j.issn.1005-0299.2000.03.010
2000-01-01
Abstract:Describle the ceramic oxide coating prepared on Ti - 6Al - 4V alloy by AC microarc oxidation in NaAlO2 solution and its morphology and microstructure observed using Scanning Electron Microscope (SEM); the analysis of composition profiles of Ti, Al, O elements in the coatings using Energy Dispersive Spectroscope (EDS), and the phase constituent of the coatings determined using X-ray diffraction (XRD) and points out the ceramic coating with about 50 μm thickness contains two layers, an outer layer and an internal layer, and the outer layer is composed of a large amount of TiAl 2O5 phase and a little rutile type TiO2 phase, but, in the internal layer, rutile becomes a main phase while the TiAl 2O5 content obviously decreases and a little TiO 1.9 phase also appears in the internal layer, and all of these phases derive from rapid solidification of the molten coatings in the microplasma discharge zone, and the high temperature and pressure processes have hardly influenced on the substrate microstructure near the coating/substrate interface.