Abstract:Ceramic coatings with aluminum titanuate (Al2TiO5) were prepared on Ti–6Al–4V alloy using pulsed bi-polar Micro-arc Oxidation (MAO). The micromorphology and phase composition of the micro-arc-oxidition ceramic coatings on the titanium alloy were characterized by X-ray powder diffraction (XRD), and scanning electron microscopy (SEM) respectively. The results revealed that the distinct discharge channels and pores on the surface of the micro-arc-oxidition coatings appeared, and these channels were connected in the molten state. The electrolyte concentration was inversely proportional to the coating hardness; additionally, the coating prepared with sodium aluminate and sodium hypophosphite concentrations of 4 g/L and 0.5 g/L, respectively, was the most refined after high-temperature sintering, and it was demonstrated to better prevent oxidation. Increasing the electrolyte concentration coincided with fluctuating coating thermal shock resistance. The thermal shock resistance of the coating respectively prepared with sodium aluminate, and the sodium hypophosphite concentrations of 4 g/L and 0.5 g/L was the highest. Additionally, the high-concentration coatings performed significantly better than the low-concentration coatings. The oxidation resistance of the coating samples was also significantly higher than that of the TC4 titanium alloy substrate. The adhesion strength between the coatings and the substrate with and without the sealing treatment was measured by tensile tests. Then, the high-temperature oxidation performance of the coating samples with and without the sealing treatment was investigated by conducting a high-temperature oxidation experiment at a calcinating temperature of 500 °C. The results indicate that the adhesion strength between the coatings and substrate was high for the as-prepared and sealed micro-arc oxidation samples regardless of whether they were calcined. The high-temperature oxidation mass increase curves for the sealed and unsealed coating samples calcined at 500 °C for 500 h revealed that the high-temperature-oxidation-induced mass increase of the coating samples sealed with a sodium silicate solution was much lower than that of the titanium alloy substrate. Thus, the sealing treatment significantly improved the high-temperature oxidation resistance of the TC4 titanium alloy. Lastly, the high-temperature oxidation behavior at 500 °C was analyzed and discussed.

Characteristics of coatings fabricated by microarc oxidation on TiAl intermetallic compound

Structure and properties characterization of ceramic coatings produced on Ti–6Al–4V alloy by microarc oxidation in aluminate solution

Characterization of Oxide Coatings Deposited on Pure Titanium by Alternating-Current Microarc Discharge in Electrolyte

Composition and structure of ceramic coatings prepared on pure titanium by alternating-current microarc oxidation

Characterization of Microarc Oxidation Coatings on Pure Titanium

Composition and Phase Structure of Microarc Oxidation Coatings Deposited on TA2 Pure Titanium

Properties Research of Ceramic Coating on AI-Li Alloy by Micro-arc Oxidation

Influence of Electrolytes on the Microstructure of Microarc Oxidation Coatings on Ti—6Al—4V Alloy

Effect of the Oxidation Time on Properties of Ceramic Coatings Produced on Ti-6Al-4V by Micro-Arc Oxidation

Preparation, characterization and mechanical properties of microarc oxidation coating formed on titanium in Al(OH) 3 colloidal solution

Microarc Oxidation Coatings Formed on Ti6Al4V in Na2SiO3 System Solution: Microstructure, Mechanical and Tribological Properties

Effects of High Temperature Oxidation on Composition and Structure of Microarc Ceramic Coating on Ti Alloy

Microstructure and Phase Composition of Microarc Oxidation Coatings Formed on Ti–6Al–4V Alloy in Aluminate Solution

High-temperature oxidation resistance of ceramic coatings on titanium alloy by micro-arc oxidation in aluminate solution

Formation of Al2O3 coatings on NiTi alloy by micro-arc oxidation method

Microstructure and Elevated Temperature Tribological Behavior of TiO2/Al2O3 Composite Ceramic Coating Formed by Microarc Oxidation of Ti6Al4V Alloy

Composition and Mechanical Properties of Hard Ceramic Coating Containing Α-Al2o3 Produced by Microarc Oxidation on Ti–6Al–4V Alloy

Microstructure and Infrared Emissivity Property of Coating Containing TiO2 Formed on Titanium Alloy by Microarc Oxidation

Microarc Oxidation Coating and High-Temperature Oxidation Resistant Property on Ti Alloy

Characteristic of Microarc Oxidized Coatings on Titanium Alloy Formed in Electrolytes Containing Aluminate and Zro2 Particles

Oxidation behavior of ceramic coatings on Ti–6Al–4V by micro-plasma oxidation