Analysis of properties of micro arc oxidation ceramic coatings for aluminum and its alloys
ZhengDong Wu,Zhaohua Jiang,Zhongping Yao,Xuelin Zhang
DOI: https://doi.org/10.3321/j.issn:1002-185X.2006.z1.037
2006-01-01
Rare Metal Materials and Engineering
Abstract:The phase composition, morphology, hardness, anti-corrosion and thermal shock resistance of the coatings produced on Al and its alloys by micro arc oxidation in sodium aluminate were investigated. The results showed that the coating consisted of two layers: a dense inner layer and a loose layer. The coating on pure Al was entirely composed of alpha-Al2O3, the coating on LC9 was composed of gamma-Al2O3, and the coating on LY12 was composed of a large amount of alpha-Al2O3 and a little gamma-Al2O3. Along the section of the coating, the hardness of the coating at both sides was lower than that in the middle, and-the maximum hardness value of the coating produced on Al, LY12 and LC9 was 33.4 GPa, 22.15 GPa and 16.8 GPa, respectively. The anti-corrosion property of the coating on LY12 was a little better than that on LC9, while the coating on Al had the worst anti-corrosion property. The thermal shock resistances of the coatings on Al, LY12 and LC9 increased in sequence. The tensile tests showed that the tension ruptures only occurred within the coatings, the bonds between the coatings and the matrixes were strong, and the bond strengths of the coatings on Al, LC9 and LY12 increased in sequence.