Abstract:The Microarc Oxidation (MAO) layer on titanium alloy was mainly composed of TiO2, and there were some defects, such as holes and cracks, which made the performance of the MAO layer not ideal. To enhance the properties of the MAO layer, titanium carbide (TiC) particles were added to the electrolyte of a phosphate–silicate system as an additive. Consequently, the MAO layers containing the TiC phase on Ti6Al4V alloy were produced. The MAO process, composition, microstructure, and hardness of the MAO layer were comprehensively analyzed. Their frictional performance was assessed under reciprocating friction conditions without lubrication. The findings suggested that added TiC particles in the electrolyte played a significant role in creating the MAO layer, enhancing its thickness. The electrolyte without TiC particles produced an MAO layer primarily composed of TiO2 in two different mineral forms (rutile and anatase). Adding TiC particles resulted in the presence of TiC within the MAO layer, thereby facilitating the formation of a reinforced oxide layer. This addition also led to an improvement in the densification of the layer and a reduction in porosity. Notably, corrosion resistance testing indicated that incorporating 6 g/L TiC into the electrolyte resulted in superior performance compared with that obtained from the base electrolyte alone by achieving 1.4 times higher corrosion resistance. Moreover, a hardness value of 690 HV for the MAO layer was attained at a content level of 9 g/L TiC, demonstrating a significant 65% enhancement compared to the base oxide layer. This finding also demonstrated significantly enhanced friction property with a wear-volume reduction to 0.81 mm3. The findings on the relationship between the preparation of the MAO layer and its structure and properties can provide valuable guidance for designing and preparing the MAO layer.

Preparation of Micro-Arc Oxidation Coating on TC11 Titanium Alloy and Study on Its Microstructure and Performance

Effect of Oxidation Time on the Structure and Properties of Ti-25Nb-3Zr-2Sn-3Mo Titanium Alloy Microarc Oxide Film Layer

Study on Structure and Properties of Microarc Oxidation Coating Formed on AM60B Magnesium Alloy

Preparation and properties of micro-arc oxidation coating on Ti75 titanium alloy

Composition and Phase Structure of Microarc Oxidation Coatings Deposited on TA2 Pure Titanium

Characterization of Microarc Oxidation Coatings on Pure Titanium

Influence of Electrolytes on the Microstructure of Microarc Oxidation Coatings on Ti—6Al—4V Alloy

Structure and properties characterization of ceramic coatings produced on Ti–6Al–4V alloy by microarc oxidation in aluminate solution

Effect of Pulse Duty Cycle and Oxidation Time on Microstructure and Properties of Micro-arc Oxidation Coatings on Ti6Al4V Alloy

Characterization of Oxide Coatings Deposited on Pure Titanium by Alternating-Current Microarc Discharge in Electrolyte

Composition and structure of ceramic coatings prepared on pure titanium by alternating-current microarc oxidation

Study on Preparation of Micro-Arc Oxidation Film on TC4 Alloy with Titanium Dioxide Colloid in Electrolyte

Microarc Oxidation Coatings Formed on Ti6Al4V in Na2SiO3 System Solution: Microstructure, Mechanical and Tribological Properties

Preparation and properties of titanium oxide film on NiTi alloy by micro-arc oxidation

Research on Growth Process and Microstructure of Microarc Oxidation Coating on Titanium

Characteristic of Microarc Oxidized Coatings on Titanium Alloy Formed in Electrolytes Containing Aluminate and Zro2 Particles

Physicochemical properties and surface topography of micro-arc oxidation coating on titanium alloy

Preparation, characterization and mechanical properties of microarc oxidation coating formed on titanium in Al(OH) 3 colloidal solution

Microarc Oxidation Coating and High-Temperature Oxidation Resistant Property on Ti Alloy

Study of Micro-arc Oxidation and Hydrothermal Treatment on the Surface of Pure Titanium

Influence of titanium carbide particles on the characteristics of microarc oxidation layer on Ti6Al4V alloy