Abstract:The mechanical properties, texture transformation, and mechanism of Al–Cu–Mn alloy during annealing were studied using three-dimensional orientation distribution function (ODF), electron backscatter diffraction (EBSD), and transmission electron microscopy (TEM). The results showed that the increase in yield strength after annealing at 200 °C is due to the decrease in the proportion of P and M textures and the increase in the proportion of Goss texture. The increase in the change rate of mechanical properties observed during annealing at 250 and 350 °C can be attributed to the higher proportion of M and P textures and the reduced proportion of Goss textures. Among them, the proportion of M texture increased significantly, and the Goss texture decreased significantly after annealing at 350 °C. This is because the structural energy density (Ev) value of the Goss texture is higher than that of the M texture at 250 °C and 350 °C. The Goss texture is in an unstable state of high energy order. The deformed Goss texture is unstable at high temperatures, leading to conversion into M and other textures. The EBSD and TEM analysis revealed that the hardness is mainly related to the change in dislocation density. When the annealing temperature is increased from 250 to 350 °C, the hardness is significantly reduced from 62 HV to 52 HV, and the dislocation density is reduced from 4.0 × 10 14 ρ/m −2 to 2.4 × 10 14 ρ/m −2 .

Mechanism of strengthening of cube texture for high purity aluminum foils by additional-annealing

Development of cube texture in multistage annealing of high purity aluminum foils

Influence Of Recrystallization Annealing On The Cube Texture In High-Purity Aluniinuni Foils

Effect of Pre-deformation and Annealing on Cube Texture in High Purity Aluminum Foils

Influence of Pre-Annealing and Additional Deformation on the Recrystallization Texture of High-Purity Aluminum Foils

Micro-process of Cube Texture Formation in High Purity Aluminum Foils by Cross Shear Rolling

Effect of Intermediate Annealing on Cubic Texture of High-purity Aluminum Foils

Influence of High Hot-Rolling Temperature and Multistage Annealing upon the Cube Texture of High Purity Aluminum Capacitor Foils

Effect of hot finishing rolling on cube texture in high purity aluminum foils

The effect of final annealing on cube texture of high-purity aluminum foils

Evolution of Microstructures and Textures of High Purity Aluminium During Rolling and Annealing

Effects of Additional Rolling and Annealing on the Cube Texture in the High-Purity Aluminum Foils for Capacitors

Increasing Cube Texture in High Purity Aluminium Foils for Capacitors

Evolution of texture and microstructure of 2E12 aluminum alloy during cold rolling and annealing

Micro-mechanism of Texture Evolution During Isochronal Annealing of As-Annealed Hot Rolled Al-Cu-Mg Sheet

Coincidence Site Lattice Boundary Mechanism for the Preferred Growth of Goss and Cube Grains During Annealing in an Al-Cu-Mg Alloy

Effect of Deformation Geometry and Friction on Shear Texture in High Purity Aluminum Foils

Study of Texture in 6016 Aluminum Alloy During Processing

Microstructure and properties of Al-4.8Cu-0.45Mn-0.19Cd-0.18Ti-0.17Zr-0.14V aluminum alloy extrusion bar

Development and Stability During High Temperature Annealing of the Cube Texture in Rolled Ni Substrate Materials

Insights of texture and microstructure evolution in the short time annealing of Al-Cu-Mg alloy at large temperature range