Abstract:In this paper, ultrafine-grained pure aluminum was first fabricated by heavy extrusion. Subsequently, the prepared samples were annealed at 350 oC for different times to tailor heterostructures with the aim of achieving strength-ductility balance. The microstructure characterization revealed that the annealed samples formed heterostructures composed of recrystallized coarse grains, retained ultrafine grains, and coarsening banded structure. Typical rolling texture components prevailed as annealing time was below 8 min. When annealing time exceeded 8 min, these texture components were gradually replaced by the Cube-oriented and random-oriented grains, and at the same time, abnormal grain growth occurred with a faster kinetic (growth exponent n similar to 3.4). Tensile tests indicated that 5-8 min annealed samples obtained a reasonable strength-ductility balance, which was higher than their counterparts predicted by the rule-of-mixture based on the recrystallization model. In addition, the macro-deformation characteristics of the heterostructured sample were comparatively studied using digital image correlation, while the micro-deformation behaviors were revealed by in-situ tension. The results showed that the heterostructured sample caused inhomogeneous deformation and significant geometrically necessary dislocations gradient at the hetero-boundaries. The loading-unloading-reloading tests found that the interaction of heterostructures induced a noteworthy hetero-deformation-induced (HDI) stress, thereby contributing to HDI strengthening.

Preparation and Annealing-Induced Structural Transition of Self-Organized Nanostripes on the Electropolished Aluminium Surface

Afm Study of Quasi-Ordered Stripe-Like Nanostructures on Surfaces of Aluminum

Self-assembled stripes on the anodic aluminum oxide by atomic force microscope observation

Formation of Self-Assembled Stripes on the Anodic Aluminum Oxide

A Facile Approach to Preparation of Nanostripes on the Electropolished Aluminum Surface

Large-area self-ordered aluminium sub-micrometre dot arrays prepared by electropolishing on polycrystalline aluminium at constant current

Crystallographic Orientation Dependence of Nanopattern Morphology and Size in Electropolished Polycrystalline and Monocrystalline Aluminum: An EBSD and SEM Study

Strengthening Mechanisms in Nanostructured High-Purity Aluminium Deformed to High Strain and Annealed

Patterning Polycrystalline Aluminum by Electropolishing at Low Voltages

Highly Ordered Nanoscale Patterns on Anodic Aluminum Oxide (AAO) Surface

Influence of Post-Annealing Treatment on the Morphology of Au Films Deposited on Liquid Surfaces

Large Strain Deformation and Annealing of Aluminium

Tailoring structures through two-step annealing process in nanostructured aluminum produced by accumulative roll-bonding

Surface-polarization-induced Formation of Amorphous Foliaceous SiO2 Helical Nanobelts

Microstructure and Characterization of Surface Nanocrystallization of Aluminum Alloy

Microstructure Evolution, Mechanical Properties and Deformation Characteristics of Ultrafine-Grained Annealed Pure Aluminum

Crystallization behavior and corrosion resistance of Al86Ni10Zr4 amorphous alloy under different annealing treatment conditions

Nanostructured Aluminium - Recovery And Recrystallization

Orientation Changes During Annealing of Nanotructured Aluminium

Quantification of Annealed Microstructures in ARB Processed Aluminum

Tailoring A Gradient Nanostructured Age-Hardened Aluminum Alloy Using High-Gradient Strain and Strain Rate