Abstract:Ordered Pt alloy electrocatalysts supported on carbon nanomaterials have attracted widespread attention, especially for the oxygen reduction reaction (ORR), due to the catalytic performance derived from their unique electronic and geometric structures. However, it is still urgent to fabricate uniform and structurally ordered Pt alloy electrocatalysts based on simple methods. Herein, a two-step direct annealing method was applied to synthesize uniform and ordered PtFe alloy nanoparticles loaded on single-wall carbon nanohorns (SWCNHs) under the protection of a thin N-doped carbon (NC) shell, which was in situ generated from the polymerization and pyrolysis of a small organic ligand, namely, aniline, during the first annealing treatment. After the second annealing treatment in a H2 atmosphere for 9 h, the obtained sample, denoted as /SWCNHs(H2-9h), exhibited uniform and ordered PtFe nanoparticles with a face-centered tetragonal (fct) structure (ordered degree: >80%, mean size: ∼5.2 nm) on the graphitic SWCNH support. Without removing the NC shell, the /SWCNHs(H2-9h) sample showed mass activity (1.53 A/mgPt at 0.9 V) and specific activity (3.61 mA/cm2 at 0.9 V) toward the ORR due to the enhanced electronic interaction derived from the ordered fct-PtFe structure. Importantly, it still retained high catalytic activity after a long-term stability test, mainly owing to the ordered fct-PtFe structure and the protection of the NC shell, which provides strong resistance toward the Fe leaching and nanoparticle aggregation, respectively. The presented strategy is generalized to fabricate different ordered PtM or Pt3M (M = Fe/Co) alloy electrocatalysts.The Supporting Information is available free of charge at <a class="ext-link" href="/doi/10.1021/acscatal.1c02434?goto=supporting-info">https://pubs.acs.org/doi/10.1021/acscatal.1c02434</a>.Additional experimental results including the structure and composition characterizations and electrochemical testing results (<a class="ext-link" href="/doi/suppl/10.1021/acscatal.1c02434/suppl_file/cs1c02434_si_001.pdf">PDF</a>)This article has not yet been cited by other publications.

Tailoring the Structure and Property of Pt-Decorated Nanoporous Gold by Thermal Annealing

Self-supporting Nanoporous Gold-Palladium Overlayer Bifunctional Catalysts Toward Oxygen Reduction and Evolution Reactions

Double Nanoporous Structure with Nanoporous PtFe Embedded in Graphene Nanopores: Highly Efficient Bifunctional Electrocatalysts for Hydrogen Evolution and Oxygen Reduction

Ph-Dependent Growth of Atomic Pd Layers on Trisoctahedral Gold Nanoparticles to Realize Enhanced Performance in Electrocatalysis and Chemical Catalysis

Nanoporous Gold: From Structure Evolution to Functional Properties in Catalysis and Electrochemistry

Surface Alloying of Pt Monolayer on Nanoporous Gold for Enhanced Oxygen Reduction

Dealloying to Nanoporous Au/Pt Alloys and Their Structure Sensitive Electrocatalytic Properties.

Electrocatalytic Activity of Bimetallic Platinum-Gold Catalysts Fabricated Based on Nanoporous Gold.

Length-Scale Modulated and Electrocatalytic Activity Enhanced Nanoporous Gold by Doping

Design and Fabrication of the High Efficient Platinum-Nanoporous Gold Catalysts

Facile Fabrication Of Ultrathin Pt Overlayers Onto Nanoporous Metal Membranes Via Repeated Cu Upd And In Situ Redox Replacement Reaction

Revealing the Role of Surface Composition on the Particle Mobility and Coalescence of Carbon-Supported Pt Alloy Fuel Cell Catalysts by in Situ Heating (S)TEM

Tuning the surface structure and phase structure of PtCu 3 nanoparticle for highly efficient electrocatalysts

Nanostructured Porous Gold for Methanol Electro-Oxidation

Native ligand carbonization renders common platinum nanoparticles highly durable for electrocatalytic oxygen reduction: annealing temperature matters

Structure Dependent Electrooxidation of Small Organic Molecules on Pt-decorated Nanoporous Gold Membrane Catalysts

Thermal Facet Healing of Concave Octahedral Pt–Ni Nanoparticles Imaged in Situ at the Atomic Scale: Implications for the Rational Synthesis of Durable High-Performance ORR Electrocatalysts

Direct Thermal Annealing Synthesis of Ordered Pt Alloy Nanoparticles Coated with a Thin N-Doped Carbon Shell for the Oxygen Reduction Reaction

Thermally stimulated structural evolution of bimetallic nanoplatelets - Changing from core-shell to alloyed to Janus nanoplatelets

Electrochemical Fabrication and Reactivation of Nanoporous Gold with Abundant Surface Steps for CO 2 Reduction