Abstract:ZrxTi1−xO4 (x=0.40–0.60) ceramics sintered without additives were prepared from powders made by the coprecipitation of metal salts from aqueous solutions in order to investigate the existence range of a homogeneous phase and the relationships between composition, microstructure and the dielectric properties. XRD, TEM, SEM, EDS, and the dielectric measurements were used to characterize the products. A homogeneous solid solution was obtained. Its crystal structure was isomorphous with ZrTiO4. The variation of the lattice parameters with TiO2 content was discussed. The optimum sintering temperature of samples was dependent of composition. TiO2 suppressed the densification and acted as a grain growth enhancer during the sintering process. With the increase in TiO2 content the relative densities of the sintered bodies decrease, while the grain sizes increase. The dielectric properties at microwave frequency (1.8 GHz) in this system, especially Q value, were poor, due to low densification, impurities and lattice defects. The dielectric constant εr and Q value exhibited a significant dependence on the relative density and composition. Both εr and Q increased with the increase in relative density, but they were primarily influenced by the composition and the effect of the relative density could be ignored when the relative density was greater than 90% theoretical. εr increased slightly with increasing TiO2 content, while Q value decreased.

Effect of composition on sinterability, microstructure and microwave dielectric properties of Zr x Ti1− x O4 (x=0.40–0.60) ceramics

Preparation, microstructure and microwave dielectric properties of ZrxTi1-xO4 (x=0.40-0.60) ceramics

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Effect of ZnO Ratio on Sintering Behavior and Microwave Dielectric Properties of BaO–ZnO–TiO2 Ceramics

Influence of Zn0.5Ti0.5NbO4 on the Structure and Microwave Dielectric Properties of ZrTiO4 Ceramics

The effect of composition on Li2(Mg0.3Zn 0.7)Ti3O8-xTiO2 microwave dielectric ceramics for low temperature co-fired ceramics technology application

Phase structure and microwave dielectric properties of Zr(Zn 1/3 Nb 2/3 ) x Ti 2−x O 6 (0.2 ≤ x ≤ 0.8) ceramics

Effects of Ti4+ substitution on microstructure and microwave dielectric properties of ZnNb2(1-x)TixO(6-3X) ceramics

Effect of TiO2 Content on the Microwave Dielectric Properties of BaO-ZnO-TiO2 Ceramics

Study on properties of nonstoichiometric Li(2+x)ZnTi3O(8+0.5x) microwave dielectric ceramics

Effect of ZnO-V2O5Co-doping on phase stability and microwave dielectric properties of ZnTiO3 ceramics

Co 2 O 3 substitution effects on the structure and microwave dielectric properties of low-firing (Zn 0.9 Mg 0.1 )TiO 3 ceramics

Phase structure and microwave dielectric properties of Zr(Zn 1/3Nb2/3)xTi2-xO6 (0.2 ≤ × ≤ 0.8) ceramics

Microstructure and Dielectric Properties of BaZr X Ti 1− X O 3 Ceramics

Low-fired microwave dielectrics in ZnO-TiO 2 ceramics doped with CuO and B 2 O 3

Effects of ZrO2 substitution on crystal structure and microwave dielectric properties of Zn0.15Nb0.3(Ti1-xZrx)0.55O2 ceramics

Structure and Microwave Dielectric Properties of Low-Temperature Sintered ZnO-TiO2 Ceramics

Microstructure and Microwave Dielectric Properties of Tio2-Doped Zn2sio4 Ceramics Synthesized Through the Sol-Gel Process

Phase structure and microwave dielectric properties of Zr(ZnNb)TiO (0.2 ≤ x ≤ 0.8) ceramics

Effects of Ti<sup>4+</sup> Substitution on Microstructure and Microwave Dielectric Properties of ZnNb<sub>2(1-x)</sub>TixO<sub>(6-3x)</sub> Ceramics