Structural Evolution of SrLaAl1−x(Zn0.5Ti0.5)xO4 Ceramics and Effects on Their Microwave Dielectric Properties

Bing Liu,Lei Li,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1039/c6tc00841k

IF: 6.4

2016-01-01

Journal of Materials Chemistry C

Abstract:The structure and microwave dielectric properties of SrLaAl1−x(Zn0.5Ti0.5)xO4 ceramics were determined in the composition range of x = 0–0.9.

What problem does this paper attempt to address?

Microwave Dielectric Properties of Temperature Stable (1-X)srlaalo4-xtio2 Composite Ceramics

Yu Hui Huang,Bing Liu,Kai Xin Song

DOI: https://doi.org/10.1016/j.ceramint.2018.08.222

IF: 5.532

2018-01-01

Ceramics International

Abstract:Dense (1-x)SrLaAlO4-xTiO(2) (x = 0, 0.05, 0.10, 0.15) composite ceramics were prepared via a standard solidstate reaction method. The effect of TiO2 addition on the sintering behavior, phase composition, microstructure and microwave dielectric properties of SrLaAlO4 ceramics were systematically investigated. The X-ray diffraction patterns revealed the co-existence of the two phases and the microstructure evolutions were observed using scanning electron microscopy analysis. The dielectric constant of the present ceramics increased from 17.5 at x= 0-21.2 at x = 0.15, and the negative temperature coefficient of resonant frequency of SrLaAlO4 ceramics (-30 ppm/degrees C) could be modified towards positive. Empirical models such as Lichtenecker logarithmic model and mixing rule were applied to explain the variation trend of the microwave dielectric properties in the present ceramics. The optimum microwave dielectric properties were achieved at x = 0.10 (epsilon(r) = 20.2, Qf = 79,500 GHz, tau(f) = 8 ppm/degrees C).
Effects of (mg1/3nb2/3) Substitution on the Structure and Microwave Dielectric Properties of Sr2TiO4 Ceramics

Bing Liu,Cheng Chao Hu,Yu Hui Huang,Kai Xin Song

DOI: https://doi.org/10.1016/j.matlet.2019.07.002

IF: 3

2019-01-01

Materials Letters

Abstract:Sr2Ti1-x(Mg1/3Nb2/3)(x)O-4 (0 <= x <= 0.4) solid solutions were synthesized by standard solid-state reaction method for the first time, and their microwave dielectric properties were systematically investigated together with the microstructure. X-ray diffraction patterns revealed the formation of solid solutions in the whole composition range, while two kinds of secondary phases started to appear when x = 0.4. With increasing x , the dielectric constant (epsilon(r)) was tuned from 42 to 26.3 and the temperature coefficient of resonant frequency (tau(f)) could be successfully modified from 130 ppm/degrees C to 46.3 ppm/degrees C. Excellent combination of microwave dielectric properties with epsilon(r) = 28.5, Qf = 83,300 GHz, and tau(f )= 53 ppm/degrees C were obtained for the x = 0.3 composition after sintering at 1500 degrees C for 3 h. (C) 2019 Elsevier B.V. All rights reserved.
Structure and Microwave Dielectric Properties of SrLa[Al1−x(Mg0.5Ti0.5)x]O4 (x = 0.2–0.8) Ceramics

Gu Yi Chen,Guang Rong Ren,Lei Li,Bing Liu,Xiang Ming Chen

DOI: https://doi.org/10.1016/j.ceramint.2017.10.142

IF: 5.532

2017-01-01

Ceramics International

Abstract:Dense SrLa[Al1−x(Mg0.5Ti0.5)x]O4 (x = 0.2–0.8) ceramics were prepared by a standard solid state sintering method. The K2NiF4–type layered perovskite structure with I4/mmm space group was revealed by XRD over the whole composition range, indicating that SrLaAlO4 and SrLa(Mg0.5Ti0.5)O4 can form infinite solid solution. The evaluation of the refined structure was investigated by Rietveld analysis of XRD and Raman spectrum. The dielectric constant (εr) and temperature coefficient of resonant frequency (τf) increased with increasing x, while the Qf value first increased and then decreased. The measured εr was significantly lower than the predicted value from Clausius-Mosotti relationship, and their difference approached 0 with increasing x, which is mainly attributed to the increasing normalized bond lengths of Sr/La-O(1) and Sr/La-O(2a) bonds. The optimal microwave dielectric properties with εr = 22.2, Qf = 89,100GHz and τf = −0.1ppm/°C were obtained for x = 0.65, indicating that SrLa[Al1−x(Mg0.5Ti0.5)x]O4 solid solution is a promising candidate as low-loss microwave dielectric ceramics.
Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Lei Wen,Lue Wen-Zhong,Wang Xiao-Chuan,Liang Jun,Jiang Jian-Jun

DOI: https://doi.org/10.3724/SP.J.1077.2009.00957

IF: 1.292

2009-01-01

Journal of Inorganic Materials

Abstract:ZnAl2O4-Mg2TiO4-CaTiO3 ceramics were prepared by the solid-state reaction. The effects of CaTiO3 on phase compositions, microstructure and microwave dielectric properties were investigated. It shows that CaTiO3 can effectively improve the sinterability of the ceramics and lower the densification temperature by about 150 degrees C. ZnAl2O4-based spinel, CaTiO3, MgTi2O5 and Zn2Ti3O8 phases are included in the ZnA(2)O(4)-Mg2TiO4-CaTiO3 system, however, Zn2Ti3O8 phase disappears when the sintering temperature is higher than 1400 degrees C. As CaTiO3 content increases, CaTiO3 phase in the sintered body raises while MgTi2O5 phase reduces. Furthermore, CaTiO3 can adjust obviously the temperature coefficient of resonant frequency of the (1-x)ZnAl2O4-xMg(2)TiO(4)(x = 0.21) ceramics. When 6mol% CaTiO3 is added to the (1-x)ZnAl2O4--xMg(2)TiO(4) (x = 0.21) system, a temperature-stable microwave dielectric ceramics sintered at 1400 degrees C with an epsilon(r) of 11.8, a Q center dot f of 88080GHz and a tau(f) of - 7.8 x 10(-6)/degrees C can be obtained.
Phase Evolution and Microwave Dielectric Properties of Novel LiAl5−xZnxO8−0.5x‐based (0 ≤ X ≤ 0.5) Ceramics

Xue-Kai Lan,Jie Li,Jia-Pu Li,Fei Wang,Wen-Zhong Lu,Xiao-Chuan Wang,Wen Lei

DOI: https://doi.org/10.1111/jace.16791

IF: 4.186

2020-01-01

Journal of the American Ceramic Society

Abstract:Novel LiAl5-xZnxO8-0.5x microwave dielectric ceramics were synthesized through a solid-state reaction route. Phase evolution of LiAl5-xZnxO8-0.5x was determined by XRD analysis. The XRD results indicated that the phase compositions had a P4(3)32 space group when 0 <= x <= 0.2 and a spinel structure when 0.3 <= x <= 0.5. The dielectric constant (epsilon(r)) of this series' solid solutions decreased with the increase in Zn doping content, which was in good agreement with the Clausius-Mossotti relation. Oxygen vacancy and the decreased degree of order degraded the quality factor (Q x f) of the two structures. The deterioration in quality factor was further verified by impedance spectroscopy. The temperature coefficient of the resonant frequency (tau(f)) decreased with the increase in x and was correlated with the unit cell volume. Finally, CaTiO3 was used as a compensation material to obtain a near-zero tau(f) of the LiAl5O8 ceramic.
Structure and microwave dielectric characteristics of Sr(La1−xSmx)2Al2O7 ceramics

Zhi Qi Yuan,Bing Liu,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1039/c6ra20776f

IF: 4.036

2016-01-01

RSC Advances

Abstract:Sr(La1−xSmx)2Al2O7 (0 ≤ x ≤ 1) ceramics were synthesized by a standard solid-state reaction method, and the microwave dielectric characteristics were investigated together with the densification behavior, microstructure and phase composition.
Effects of CaTiO3 on Microstructures and Properties of (1-x)ZnAl2O4-xMg2TiO4(x=0.21) Microwave Dielectric Ceramics: Effects of CaTiO3 on Microstructures and Properties of (1-x)ZnAl2O4-xMg2TiO4(x=0.21) Microwave Dielectric Ceramics

Wen LEI,Lü Wen-Zhong,Xiao-Chuan WANG,Jun LIANG,Jian-Jun JIANG

DOI: https://doi.org/10.3724/SP.J.1077.2009.00957

IF: 1.292

2009-01-01

Journal of Inorganic Materials

Abstract:ZnAl2O4-Mg2TiO4-CaTiO3 ceramics were prepared by the solid-state reaction. The effects of CaTiO3 on phase compositions, microstructure and microwave dielectric properties were investigated. It shows that CaTiO3 can effectively improve the sinterability of the ceramics and lower the densification temperature by about 150 degrees C. ZnAl2O4-based spinel, CaTiO3, MgTi2O5 and Zn2Ti3O8 phases are included in the ZnA(2)O(4)-Mg2TiO4-CaTiO3 system, however, Zn2Ti3O8 phase disappears when the sintering temperature is higher than 1400 degrees C. As CaTiO3 content increases, CaTiO3 phase in the sintered body raises while MgTi2O5 phase reduces. Furthermore, CaTiO3 can adjust obviously the temperature coefficient of resonant frequency of the (1-x)ZnAl2O4-xMg(2)TiO(4)(x = 0.21) ceramics. When 6mol% CaTiO3 is added to the (1-x)ZnAl2O4--xMg(2)TiO(4) (x = 0.21) system, a temperature-stable microwave dielectric ceramics sintered at 1400 degrees C with an epsilon(r) of 11.8, a Q center dot f of 88080GHz and a tau(f) of - 7.8 x 10(-6)/degrees C can be obtained.
Structural Evolution and Its Effects on Dielectric Loss in Sr1+xSm1−xAl1−xTixO4 Microwave Dielectric Ceramics

Min,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1111/j.1551-2916.2011.04408.x

IF: 4.186

2011-01-01

Journal of the American Ceramic Society

Abstract:The structural evolution of Sr1−xSm1+xAl1−xTixO4 (x=0, 0.05, 0.10, and 0.15) microwave dielectric ceramics was investigated together with its effects on dielectric loss. Through the analysis of Rietveld refinement of powder X-ray diffraction, the normalized bond length and normalized bond valence showed an abnormal variation of Sr/Sm–O(2b) and Al/Ti–O(2) bonds from x=0.10 to x=0.15. The abnormal variation related to these bonds in Raman spectra and IR reflectivity spectra was observed. IR reflectivity spectra were calculated by the classical oscillator model fitting to evaluate the intrinsic loss. The calculated Q × f value and the measured ones both decreased as x increased, and a sharp decrease from x=0.10 to x=0.15 was observed. The decreased tolerance factor should be responsible for the decreased Q × f value. Moreover, the abnormal evolution of Sr/Sm–O(2)–Al/Ti bonding that can cause an extra local stress should be responsible for the sharp decrease from x=0.10 to x=0.15 in Q × f value.
Structure Evolution and Enhanced Microwave Dielectric Characteristics of (Sr1−xCax)La2Al2O7 Ceramics

lei yi,lei li,xiao qiang liu,xiang ming chen

DOI: https://doi.org/10.1111/jace.13145

IF: 4.186

2014-01-01

Journal of the American Ceramic Society

Abstract:(Sr1-xCax)La2Al2O7 (0.1x0.5) ceramics were prepared by a standard solid-state reaction method. Their densification behavior and microwave dielectric properties were investigated together with the structural evolution. X-ray diffraction analysis indicated that the major phase of Ruddlesden-Popper structure with n=2 was obtained for all the compositions investigated here. Partial Ca substitution improved the sintering behavior of SrLa2Al2O7 ceramics. More importantly, microwave dielectric characteristics were enhanced in (Sr1-xCax)La2Al2O7 ceramics with compositions of x=0.1-0.3. The stacking fault was confirmed by TEM observation in the present ceramics, and the microwave dielectric loss was influenced by it. The best combination of microwave dielectric characteristics was achieved for the composition of x=0.1: epsilon(r) = 19.9, Qf=135400GHz and (f)=-18.5ppm/degrees C.
Structural Evolution and Microwave Dielectric Properties of xZn0.5Ti0.5NbO4-(1- x)Zn0.15Nb0.3Ti0.55O2 Ceramics.

Shuren Zhang,Hongcheng Yang,E. Li,Xing Zhang,Hongyu Yang

DOI: https://doi.org/10.1021/acs.inorgchem.8b00873

IF: 4.6

2018-06-29

Inorganic Chemistry

Abstract:Structure and microwave properties of xZn0.5Ti0.5NbO4-(1 - x)Zn0.15Nb0.3Ti0.55O2 ceramics in the range of x = 0.0-1.0 were investigated. Rietveld refinement analysis and Raman spectra show that rutile- and orthorhombic-type solid solutions formed at 0-0.2 and 0.65-1, a composite at 0.2-0.64. In the solid solution regions, chemical bonds are enlarged. In this case, the Zn/Ti/Nb-O1 bond covalency and bond susceptibility are reduced, and lattice energy and thermal expansion coefficient increase along with x increases, which is mainly responsible for the development of microwave dielectric properties. Furthermore, far-infrared spectra and a classical oscillator model were used to discuss the intrinsic dielectric properties in detail. Temperature stable ceramic was obtained for x = 0.516: εr ∼ 46.11, Q × f ∼ 27 031 GHz, and τf ∼ -1.51 ppm/°C, which is promising for microwave applications.

Medicine,Materials Science,Physics,Chemistry
Structural Evolution and Microwave Dielectric Properties in Sr2(Ti1-xSnx)O4 Ceramics

Bing Liu,Yu Hui Huang,Kai Xin Song,Lei Li,Xiang Ming Chen

DOI: https://doi.org/10.1016/j.jeurceramsoc.2018.04.029

IF: 5.7

2018-01-01

Journal of the European Ceramic Society

Abstract:The structure and microwave dielectric properties of Sr-2(Ti1-xSnx)O-4 ceramics were determined in the entire composition range of x = 0-1.0. X-ray diffraction patterns and Raman spectra indicated a composition-induced onset of octahedral tilting at x = 0.75, and the crystal structure transformed from tetragonal (I4/mmm) to orthorhombic (Pccn). An obvious change of grain morphology was observed in the phase transformation region as well. The variations of the microwave dielectric properties with composition were systematically investigated and the effect of octahedral tilting on the evolution of tau(f) value was emphasized. Moreover, the relationship between tau(c) and tolerance factor of the present ceramics was revealed and compared with the empirical rule in perovskite structure. The role of tolerance factor in designing the materials with required performance was highlighted.
Structure and Microwave Dielectric Characteristics of Sr-2[Ti1-x(Al0.5Nb0.5)(x)]O-4 (x <= 0.50) Ceramics

Iqra Hameed,Shu Ya Wu,Lei Li,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1111/jace.16510

IF: 4.186

2019-01-01

Journal of the American Ceramic Society

Abstract:Sr-2[Ti1-x(Al0.5Nb0.5)(x)]O-4 (x = 0, 0.10, 0.25, 0.30, 0.5) ceramics were synthesized by a standard solid-state reaction process. Sr-2[Ti1-x(Al0.5Nb0.5)(x)]O-4 solid solutions with tetragonal Ruddlesdon-Popper (R-P) structure in space group I4/mmm were obtained within x <= 0.50, and only minor amount (1-2 wt%) of Sr3Ti2O7 secondary phase was detected for the compositions x >= 0.25. The temperature coefficient of resonant frequency tau(f) of Sr-2[Ti1-x(Al0.5Nb0.5)(x)]O-4 ceramics was significantly improved from 132 to 14 ppm/degrees C correlated with the increase in degree of covalency (%) with increasing x. The dielectric constant e(r) decreased linearly with increasing x, while high Qf value was maintained though it decreased firstly. The variation tendency of Qf value was dependent on the trend of packing fraction combined with the microstructure. Good combination of microwave dielectric properties was achieved for x = 0.50: e(r) = 25.1, Qf = 77 580 GHz, tau(f) = 14 ppm/degrees C. The present ceramics could be expected as new candidates of ultra-high Q microwave dielectric materials without noble element such as Ta.
Structural Evolution and Enhanced Microwave Dielectric Properties in Sr 2+ /ti 4+ Co-Substituted SrNd 2 Al 2 O 7 Ceramics

Bing Liu,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1016/j.jallcom.2018.05.117

IF: 6.2

2018-01-01

Journal of Alloys and Compounds

Abstract:Dense Sr1+2xNd2-2xAl2-2xTi2xO7 (x = 0, 0.05, 0.10, 0.15) ceramics were prepared via a standard solid state reaction method, and the structure and phase composition were investigated together with their effects on the microwave dielectric properties. The major phase with n = 2 Ruddlesden-Popper structure was confirmed from the X-ray diffraction patterns, while two ineluctable secondary phases were also observed. With increasing x, the dielectric constant er increased monotonously from 21.4 to 23.3, and the temperature coefficient of resonant frequency t(f) was tuned from -6.1 ppm/degrees C to -1.0 ppm/degrees C. The Qf value was improved from 63,700 GHz at x = 0.0 to 76,500 GHz at x 1/4 0.10 and turned to decrease thereafter. The drop of Qf value at x = 0.15 could be attributed to the increased amount of secondary phase, where stacking faults were also detected from the TEM images. Moreover, infrared reflectivity spectra analyses were applied to further understand the variation of intrinsic dielectric properties. The optimum microwave dielectric properties were achieved at x = 0.10: e(r) = 22.5, Qf = 76,500 GHz, t(f) = -1.5 ppm/degrees C. (C) 2018 Elsevier B.V. All rights reserved.
Structure and Microwave Dielectric Characteristics of Solid Solutions in SrNdAlO4‐Sr2TiO4 System

Chao Zhang,Lei Yi,Lei Li,Xiang Ming Chen

DOI: https://doi.org/10.1111/ijac.12011

2013-01-01

International Journal of Applied Ceramic Technology

Abstract:Dense ceramics in SrNdAlO4‐Sr2TiO4 system were synthesized by a solid‐state reaction method, and their microstructures and microwave dielectric characteristics were investigated. The K2NiF4‐type solid solutions with general formula Sr1+xNd1‐xAl1‐xTixO4 were obtained in the entire composition range (0.05 ≤ x ≤ 0.9). With increasing x, the dielectric constant εr increased from 19.2 to 25, and the temperature coefficient of resonant frequency τf was adjusted from −16.7 to 24.6 ppm/°C. The significantly improved Qf value was achieved in the present ceramics with increasing x, and it reached a maximum at x = 0.6. The best combination of microwave dielectric characteristics was achieved at x = 0.6 (εr = 23.6, Qf = 86,300 GHz, τf = 10.9 ppm/oC). The reduced interlayer polarization with Sr/Ti cosubstitution in SrNdAlO4 contributed to the improved Qf, while the decreased tolerance factor and increased inner stress brought the negative effects.
Effects of Structural Transition on Microwave Dielectric Properties of Sr-3(Ti1-xSnx)(2)O-7 Ceramics

Bing Liu,Yu Hui Huang,Hadi Barzegar Bafrooei,Kai Xin Song,Lei Li,Xiang Ming Chen

DOI: https://doi.org/10.1016/j.jeurceramsoc.2019.07.046

IF: 5.7

2019-01-01

Journal of the European Ceramic Society

Abstract:Sr-3(Ti1-xSnx)(2)O-7 (x = 0-1.0) ceramics were prepared via a standard solid-state reaction method. X-ray diffraction patterns and Rietveld refinement results indicated a composition induced onset of octahedral tilting when x > 0.2, and the crystal structure transformed in sequence: tetragonal (14/mmm) -> coexistence of tetragonal and orthorhombic (I4/mmm + Amam) -> orthorhombic (Amam). The tau(f) value could be successfully tuned towards zero and the effects of octahedral tilting on the evolution of tau(f) value were emphasized. Meanwhile, the role of tolerance factor in tailoring the resultant z of the present ceramics was revealed and compared with the empirical rule for complex perovskites. Qf value decreased monotonously with increasing x, which could be elucidated by the variations of extrinsic parameters and intrinsic dielectric loss extrapolated from the infrared reflectivity spectra. The optimum microwave dielectric properties were achieved at x = 0.8 (epsilon(r) = 18.6, Q(f) = 45,250 GHz, tau(f) = -14 ppm/degrees C).
Structure and Microwave Dielectric Properties of Solid Solution in SrLaAlO4-Sr2TiO4 System

Min Mao,Xiang Ming Chen,Xiao Qiang Liu

DOI: https://doi.org/10.1111/j.1551-2916.2011.04627.x

IF: 4.186

2011-01-01

Journal of the American Ceramic Society

Abstract:Ceramics in (1− x ) SrLaAlO 4 ‐ x Sr 2 TiO 4 system were synthesized in the entire range of 0 ≤ x ≤ 1 by a standard solid‐state reaction method. X‐ray diffraction patterns revealed a single solid solution phase Sr 1+ x La 1− x Al 1− x Ti x O 4 with K 2 NiF 4 ‐type structure. The cell refinement showed the linear variation of lattice parameters a, c, and cell volume. With increasing x , ε r increased from 17.6 to 31.0, whereas τ f was tuned from −32 to 122 ppm/ o C. The Qf value first increased and then decreased with increasing x due to the result of competition balance between the effect of layer mismatch and interlayer polarization. The degradation of Qf value in the vicinity of x = 0.2 could be attributed to the compositional fluctuation and inhomogeneity originated from the positive mixing enthalpy Δ H mix , which could be confirmed by TEM observation. The best combination of microwave dielectric characteristics was achieved at x = 0.4: ε r = 18.5, Qf = 95 000 GHz, τ f = −8.9 ppm/ o C.
Structural Evolution and Microwave Dielectric Properties of xZn0.5Ti0.5NbO4-(1–x)Zn0.15Nb0.3Ti0.55O2 Ceramics

Hongyu Yang,Shuren Zhang,Hongcheng Yang,Xing Zhang,Enzhu Li

DOI: https://doi.org/10.1021/acs.inorgchem.8b00873

IF: 4.6

2018-01-01

Inorganic Chemistry

Abstract:Structure and microwave properties of xZn0.5Ti0.5NbO4-(1 - x)Zn0.15Nb0.3Ti0.55O2 ceramics in the range of x = 0.0-1.0 were investigated. Rietveld refinement analysis and Raman spectra show that rutile- and orthorhombic-type solid solutions formed at 0-0.2 and 0.65-1, a composite at 0.2-0.64. In the solid solution regions, chemical bonds are enlarged. In this case, the Zn/Ti/Nb-O1 bond covalency and bond susceptibility are reduced, and lattice energy and thermal expansion coefficient increase along with x increases, which is mainly responsible for the development of microwave dielectric properties. Furthermore, far-infrared spectra and a classical oscillator model were used to discuss the intrinsic dielectric properties in detail. Temperature stable ceramic was obtained for x = 0.516: er ∼ 46.11, Q × f ∼ 27 031 GHz, and τf ∼ -1.51 ppm/°C, which is promising for microwave applications.
Structure Evolution and Microwave Dielectric Characteristics of Ca[(Alxga0.5-Xnb0.5)(0.5)Ti-0.5]O-3 Ceramics

Song Lin Zhang,Pian,Xiao Qiang Liu,Xiang Ming Chen

DOI: https://doi.org/10.1016/j.jallcom.2016.09.088

IF: 6.2

2016-01-01

Journal of Alloys and Compounds

Abstract:The microwave dielectric characteristics of Ca[(AlxGa0.5-xNb0.5)(0.5)Ti-0.5]O-3 (x - 0, 0.1, 0.2, 0.4, 0.5) ceramics were investigated together with the structure evolution. Distorted perovskite structure in space group Pbnm with b(-)b(-)c(+) tilting was determined for the present solid solutions, where the microstructures were remarkably affected by Al-content. Owing to the Al-substitution which was accompanied by the subdued octahedral tilting, the Qf value reached up to 40,000 GHz with increasing x, the dielectric constant (epsilon(r)) remained at around 50, and the temperature coefficient of resonant frequency (tau(f)) could be adjusted to near zero. Low-loss temperature-stable microwave dielectric ceramics with medium dielectric constant were obtained at x = 0.2-0.5, which exhibited Qf values of 35,900-40,000 GHz, epsilon(r) of 49.2-53.4, and tf of 0.6-3.5 ppm/degrees C. (C) 2016 Elsevier B.V. All rights reserved.
Influence of Zn0.5Ti0.5NbO4 on the Structure and Microwave Dielectric Properties of ZrTiO4 Ceramics

Qiu Yang,Enzhu Li,Hongyu Yang,Hongcheng Yang,Qingyu Wen,Ying Yuan,Shuren Zhang

DOI: https://doi.org/10.1016/j.ceramint.2019.10.182

IF: 5.532

2020-01-01

Ceramics International

Abstract:In this work, xZn(0.5)Ti(0.5)NbO(4)-(1-x) ZrTiO4 (0.1 <= x <= 0.5) ceramics were prepared through the traditional solid-state route. The microstructure, phase evolution and crystallographic variations were investigated in detail. An orthorhombic structure solid solution was formed with the composition of Zr1-xZn0.5Ti1-0.5xNbxO4 (0.1 <= x <= 0.5). Variations of lattice parameters were responsible for the opposite movement of different XRD peaks as increasing x value. Chemical bond theories include that bond ionicity, bond susceptibility, lattice energy, bond energy and linear thermal expansion coefficient are correlated with dielectric properties. Temperature stable ceramics were obtained when x = 0.2 with excellent dielectric performances: Q x f = 26741 GHz, epsilon(r) = 41.93 and tau(f) = - 2.3 ppm/degrees C.
Phase structure and microwave dielectric properties of Zr(Zn 1/3Nb2/3)xTi2-xO6 (0.2 ≤ × ≤ 0.8) ceramics

Bin Tang,Shengquan Yu,Hetuo Chen,Shuren Zhang,Xiaohua Zhou

DOI: https://doi.org/10.1007/s10854-012-0955-7

2013-01-01

Abstract:The phase structure, morphology and microwave dielectric properties of Zr(Zn1/3Nb2/3)(x)Ti2-xO6 (0.2 a parts per thousand currency sign x a parts per thousand currency sign 0.8) ceramics were investigated as a function of the amount of (Zn1/3Nb2/3)(4+) substitution by the solid-state reaction technique. X-ray diffraction analysis showed the co-existence of the solid solution ZrTiO4 (x = 0.2) or ZrTi2O6(x = 0.4-0.5) as the main phase and TiO2 as the second phase, and the single-phase region for substituted ZrTi2O6 was obtained with x a parts per thousand yen 0.5. As increasing x from 0.2 to 0.8, the grain growth was promoted, moreover the dielectric constant epsilon(r) and the temperature coefficient of resonant frequency tau(f) dropped from 53.8 to 39.2 and from +106.2 to -25.5 ppm/A degrees C respectively, and the Q x f values increased from 33,200 to 43,200 GHz. Ceramics with good microwave dielectric properties: epsilon(r) = 41.7, Q x f = 42,100 GHz and tau(f) = -15.5 ppm/A degrees C was obtained at x = 0.6.

Structural Evolution of SrLaAl1−x(Zn0.5Ti0.5)xO4 Ceramics and Effects on Their Microwave Dielectric Properties

Microwave Dielectric Properties of Temperature Stable (1-X)srlaalo4-xtio2 Composite Ceramics

Effects of (mg1/3nb2/3) Substitution on the Structure and Microwave Dielectric Properties of Sr2TiO4 Ceramics

Structure and Microwave Dielectric Properties of SrLa[Al1−x(Mg0.5Ti0.5)x]O4 (x = 0.2–0.8) Ceramics

Effects Of Catio(3)On Microstructures And Properties Of (1-X) Znal2o4-Xmg(2) Tio4 (X=0.1) Microwave Dielectric Ceramics

Phase Evolution and Microwave Dielectric Properties of Novel LiAl5−xZnxO8−0.5x‐based (0 ≤ X ≤ 0.5) Ceramics

Structure and microwave dielectric characteristics of Sr(La<sub>1−x</sub>Sm<sub>x</sub>)<sub>2</sub>Al<sub>2</sub>O<sub>7</sub> ceramics

Structural Evolution and Its Effects on Dielectric Loss in Sr1+xSm1−xAl1−xTixO4 Microwave Dielectric Ceramics

Structure Evolution and Enhanced Microwave Dielectric Characteristics of (Sr1−xCax)La2Al2O7 Ceramics

Structural Evolution and Microwave Dielectric Properties of xZn0.5Ti0.5NbO4-(1- x)Zn0.15Nb0.3Ti0.55O2 Ceramics.

Structural Evolution and Microwave Dielectric Properties in Sr2(Ti1-xSnx)O4 Ceramics

Structure and Microwave Dielectric Characteristics of Sr-2[Ti1-x(Al0.5Nb0.5)(x)]O-4 (x <= 0.50) Ceramics

Structural Evolution and Enhanced Microwave Dielectric Properties in Sr 2+ /ti 4+ Co-Substituted SrNd 2 Al 2 O 7 Ceramics

Structure and Microwave Dielectric Characteristics of Solid Solutions in SrNdAlO4‐Sr2TiO4 System

Effects of Structural Transition on Microwave Dielectric Properties of Sr-3(Ti1-xSnx)(2)O-7 Ceramics

Structure and Microwave Dielectric Properties of Solid Solution in SrLaAlO4-Sr2TiO4 System

Structural Evolution and Microwave Dielectric Properties of <i>x</i>Zn<sub>0.5</sub>Ti<sub>0.5</sub>NbO<sub>4</sub>-(1–<i>x</i>)Zn<sub>0.15</sub>Nb<sub>0.3</sub>Ti<sub>0.55</sub>O<sub>2</sub> Ceramics

Structure Evolution and Microwave Dielectric Characteristics of Ca[(Alxga0.5-Xnb0.5)(0.5)Ti-0.5]O-3 Ceramics

Influence of Zn0.5Ti0.5NbO4 on the Structure and Microwave Dielectric Properties of ZrTiO4 Ceramics

Phase structure and microwave dielectric properties of Zr(Zn 1/3Nb2/3)xTi2-xO6 (0.2 ≤ × ≤ 0.8) ceramics