Structure And Microwave Dielectric Characteristics Of Ca1+Xnd1-Xal1-Xtixo4 Ceramics
Hong Xia Yuan,Xiang Ming Chen,Min Min Mao
DOI: https://doi.org/10.1111/j.1551-2916.2009.03216.x
IF: 4.186
2009-01-01
Journal of the American Ceramic Society
Abstract:CaNdAlO4 microwave dielectric ceramics were modified by Ca/Ti co-substitution, and their dielectric characteristics were evaluated along with their structure and microstructures. Ca1+xNd1-xAl1-xTixO4 (x=0, 0.025, 0.05, 0.10, 0.15, 0.20) ceramics with the relative density of over 95% theoretical density were obtained by sintering at 1400 degrees-1450 degrees C in air for 3 h, where the K2NiF4-type solid solution single phase was determined from the compositions of x<0.20, while a small amount of CaTiO3 secondary phase was detected for x=0.20. With Ca/Ti co-substitution in CaNdAlO4 ceramics, the dielectric constant (epsilon(r)) increased with increasing x, and the temperature coefficient of resonant frequency (tau(f)) was adjusted from negative to positive, while the Q x f(0) value increased significantly at first and reached an extreme value at x=0.025 and the maximum at x=0.15. The best combination of microwave dielectric characteristics were achieved at x=0.15 (epsilon(r)=19.5, Q x f(0)=93 400 GHz, tau(f) = -2 ppm/degrees C). The improvement of the Q x f(0) value primarily originated from the reduced interlayer polarization with Ca/Ti co-substitution, while the decreased tolerance factor, the subsequent increased interlayer stress, and the appearance of CaTiO3 secondary phase brought negative effects upon the Q x f(0) value.