Structure evolution and improved microwave dielectric characteristics in CaTi1-x(Al0.5Nb0.5)xO3 ceramics
Iqra Hameed,Xiao Qiang Liu,Lei Li,Mei Ying Liu,Xiang Ming Chen
DOI: https://doi.org/10.1016/j.jallcom.2020.155435
IF: 6.2
2020-12-01
Journal of Alloys and Compounds
Abstract:Enhanced microwave dielectric characteristics in (Al0.5Nb0.5)-co-substituted CaTiO3 ceramics were examined by means of structure evolution. CaTi1-x (Al0.5Nb0.5) x O3 solid solutions with orthorhombic structure in space group Pbnm were attained throughout the entire composition range x ≤ 0.75. The near-zero temperature coefficient of resonant frequency τ f and significantly improved quality factor Qf value were achieved, while a tunable medium dielectric constant ϵ r was achieved in the present ceramics. τ f was tuned from 750 ppm/°C to 5 ppm/°C and became −80 ppm/°C finally (at x = 0.75), the Qf was first increased from 11,500 GHz up to 49,700 GHz due to the stable perovskite structure with increased bond strength and degree of covalency (%) and then slightly decreased to 43,100 GHz at x = 0.75. The best combination of significantly improved microwave dielectric characteristics was achieved at x = 0.45 (ϵ r = 55.1, Qf = 49,700 GHz, τ f = 5 ppm/°C). The present ceramics showed the great application potential in future wireless communication systems.
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering