Abstract:(Cu,C)Ba2Ca3Cu4Oy is a nontoxic cuprate superconducting material with a superconducting transition temperature of about 116 K. Recently, it was found that bulk samples of this material synthesized under high pressure hold the highest irreversibility line among all the superconductors, which is very promising for its application in the liquid nitrogen temperature field. In this work, high-temperature (Cu,C)Ba2Ca3Cu4Oy superconducting films with large irreversible fields were prepared on SrLaAlO4(00l) substrates by pulsed laser deposition. The substrate temperature during deposition proved to be the most important parameter determining the morphology and critical temperature of the superconductors, with 680 °C considered to be the optimum temperature. X-ray diffraction (XRD) results showed that the (Cu,C)Ba2Ca3Cu4Oy films prepared under optimal conditions exhibited epitaxial growth with the a-axis perpendicular to the film surface and the b- and c-axes parallel to the substrate, with no evidence of any other orientation. In addition, resistivity measurements showed that the onset transition temperature (Tconset) was approximately 116 K, the zero-resistance critical temperature (Tc0) was around 53 K, and the irreversible field (Hirr) was about 9 T at 37 K for (Cu,C)Ba2Ca3Cu4Oy films under optimal temperature. This is the first example of the successful growth of superconducting (Cu,C)Ba2Ca3Cu4Oy films on SrLaAlO4(00l) substrates. This will facilitate high-performance applications of (Cu,C)Ba2Ca3Cu4Oy superconducting materials in the liquid nitrogen temperature field.

Growth of HgBa2CaCu2Oy films with a buffer layer

High Tc Superconducting HgBa2CaCu2Oy Films Growth on the YZrO2 Substrates with YBa2Cu3O7 Buffer Layers

Surface Structure and Transport Properties of <font>YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub></font> Using <font>La<sub>2/3</sub>Ca<sub>1/3</sub>MnO<sub>3</sub></font> as Buffer

Surface Structure and Transport Properties of Yba2cu3o7-Delta Using La2/3ca1/3mno3 As Buffer

Epitaxial growth of Gd 2 Zr 2 O 7 /Y 2 O 3 buffer layers for YBa 2 Cu 3 O 7− δ coated conductors

Enhancing superconductivity of ultrathin YBa<sub>2</sub>Cu<sub>3</sub>O<sub>7-δ</sub> films by capping non-superconducting oxides*

Preparation and Superconducting Properties of the (cu,c)ba2ca3cu4o11+y Films with Zero-Resistance Transition Temperature of 96 K

Thickness Effect of Gd2Zr2O7 Buffer Layer on Performance of YBa2Cu3O7−δ Coated Conductors

Y-Ba-Cu-O Superconducting Films Grown on (100) Magnesia and Sapphire Substrates by A Melt Growth Method Without Crucible

GROWING AND STUDY OF Eu-Cu-O BUFFER LAYER AND Y-Ba-Cu-O TIN FILM

Preparation of Yba2cu3o7-X Superconducting Thin-Films over Large Area Substrates

Effect of Hf Addition on Critical Current Density of (y,eu)ba 2 Cu 3.6 O 7-Δ Thin Films Prepared by Trifluoroacetate Metal Organic Deposition

High T C Superconductivity in LnBa 2 Cu 3 O 7- Y (ln=yb, Er) Single Crystal with Large Size

Superconducting Characteristics and Epitaxial-Growth Analyses of YBa2Cu3O7−x Thin Films by Direct-Current Magnetron Sputtering

Epitaxial growth of YBCO thin films on LaAlO3 substrate with CeO2 buffer layer

Fabrication of Highly -Axis Oriented Hg - Pb - Ba - Ca - Cu - O Thin Films

Growth and characterization of HgBa2CaCu2O6+d and HgBa2Ca2Cu3O8+d crystals

High-Temperature (Cu,C)Ba2Ca3Cu4Oy Superconducting Films with Large Irreversible Fields Grown on SrLaAlO4 Substrates by Pulsed Laser Deposition

Growth and Characterization of HgBa2CaCu2O6+δ and HgBa2…

Epitaxial Growth of BaHfO3 Buffer Layer and Its Structure Degeneration Analysed by Raman Spectrum.

Epitaxial Growth and Characterization of Dual-Sided Y2O3 Buffer Layer for Superconducting Coated Conductors