High-Temperature (Cu,C)Ba2Ca3Cu4Oy Superconducting Films with Large Irreversible Fields Grown on SrLaAlO4 Substrates by Pulsed Laser Deposition

Yugang Li,Zhiyong Liu,Ping Zhu,Jinyu He,Chuanbing Cai
DOI: https://doi.org/10.3390/cryst14060514
IF: 2.7
2024-05-29
Crystals
Abstract:(Cu,C)Ba2Ca3Cu4Oy is a nontoxic cuprate superconducting material with a superconducting transition temperature of about 116 K. Recently, it was found that bulk samples of this material synthesized under high pressure hold the highest irreversibility line among all the superconductors, which is very promising for its application in the liquid nitrogen temperature field. In this work, high-temperature (Cu,C)Ba2Ca3Cu4Oy superconducting films with large irreversible fields were prepared on SrLaAlO4(00l) substrates by pulsed laser deposition. The substrate temperature during deposition proved to be the most important parameter determining the morphology and critical temperature of the superconductors, with 680 °C considered to be the optimum temperature. X-ray diffraction (XRD) results showed that the (Cu,C)Ba2Ca3Cu4Oy films prepared under optimal conditions exhibited epitaxial growth with the a-axis perpendicular to the film surface and the b- and c-axes parallel to the substrate, with no evidence of any other orientation. In addition, resistivity measurements showed that the onset transition temperature (Tconset) was approximately 116 K, the zero-resistance critical temperature (Tc0) was around 53 K, and the irreversible field (Hirr) was about 9 T at 37 K for (Cu,C)Ba2Ca3Cu4Oy films under optimal temperature. This is the first example of the successful growth of superconducting (Cu,C)Ba2Ca3Cu4Oy films on SrLaAlO4(00l) substrates. This will facilitate high-performance applications of (Cu,C)Ba2Ca3Cu4Oy superconducting materials in the liquid nitrogen temperature field.
materials science, multidisciplinary,crystallography
What problem does this paper attempt to address?
The problem that this paper attempts to solve is: to grow high - quality high - temperature superconducting material (Cu,C)Ba₂Ca₃Cu₄Oᵧ thin films on SrLaAlO₄(00l) single - crystal substrates by pulsed - laser deposition (PLD) technology, so as to realize its application in high irreversible field (Hirr) within the liquid - nitrogen temperature range. Specifically, the researchers focus on how to improve key performance indicators such as the crystallization quality, superconducting transition temperature (Tc), and irreversible field (Hirr) of the thin films by optimizing parameters such as the deposition temperature, thus providing a basis for the high - performance application of (Cu,C)Ba₂Ca₃Cu₄Oᵧ materials. The research background points out that (Cu,C)Ba₂Ca₃Cu₄Oᵧ is a non - toxic copper - oxide superconducting material with a superconducting transition temperature of about 116 K. Recent research has found that this material exhibits the highest irreversible line in bulk samples synthesized under high pressure, which gives it broad application prospects in the liquid - nitrogen temperature field. However, since these bulk samples can only be synthesized under high - pressure conditions and are usually only a few millimeters in size, their large - scale applications are limited. Therefore, it is particularly important to develop a method for preparing (Cu,C)Ba₂Ca₃Cu₄Oᵧ thin films with excellent properties under normal conditions. The experimental results in the paper show that at the optimal deposition temperature of 680 °C, the (Cu,C)Ba₂Ca₃Cu₄Oᵧ thin films exhibit good epitaxial growth characteristics, with the a - axis perpendicular to the film surface and the b - axis and c - axis parallel to the substrate. In addition, resistivity measurements indicate that the onset transition temperature (Tconset) of the thin films is about 116 K, the zero - resistance critical temperature (Tc0) is about 53 K, and the irreversible field (Hirr) at 37 K is about 9 T. These results lay the foundation for the high - performance application of (Cu,C)Ba₂Ca₃Cu₄Oᵧ thin films within the liquid - nitrogen temperature range.