Zirconia ultrafiltration membranes on silicon carbide substrate: microstructure and water flux
Shuang Li,Chuncheng Wei,Peng Wang,Peiling Gao,Lijuan Zhou,Guangwu Wen
DOI: https://doi.org/10.1016/j.jeurceramsoc.2020.04.020
IF: 5.7
2020-09-01
Journal of the European Ceramic Society
Abstract:<p>This study reported the preparation of ZrO<sub>2</sub>/SiC ceramic membrane with silicon carbide as the substrate and intermediate layers and zirconia as the selective layer. The substrate and intermediate layers were sintered by evaporation-condensation process at 2200 and 1900 ℃, respectively. After sintering, the intermediate layer presented layer thickness of 50 μm, pore size of 0.87 μm and pure water permeability of 2140 L/(m<sup>2</sup>·h). The selective lay was deposited on the silicon carbide substrate by dip-coating method and then sintered in the temperature range from 800 to 1000 ℃. For the membrane coated by one dip-coating cycle and sintered at 800 ℃, it presented average pores of 82 nm and water flux of 850 L/(m<sup>2</sup>·h). Due to the exclusion of low-melting oxides during sintering, the ZrO<sub>2</sub>/SiC ceramic membrane can satisfy the separation and purification of chemical corrosion and high temperature wastewater.</p>
materials science, ceramics