Abstract:The reduction processes of Fe-Mo-O catalysts with different Fe/Mo atomic ratios were studied by means of temperature-programmed reduction (TPR). In particular, the reduction process of a sample with an Fe/Mo ratio of 0.29 was investigated in detail in combination with in situ Mössbauer spectroscopy (MBS) and X-ray diffraction (XRD). Five peaks are observed in the TPR profile of this sample with peak temperatures at 853, 910, 952, 1014, and 1233 K, respectively, indicating that the reduction of the catalyst proceeds via five stages. MBS and XRD showed that the phases in the sample are MoO3 and Fe2(MoO4)3 before TPR. At the first TPR peak (853 K), Fe2(MoO4)3 was completely transformed into β-FeMoO4 and Mo4O11, while MoO3 was not affected. The β-FeMoO4 phase that formed can convert to α-FeMoO4 when the reduced sample is exposed to air at room temperature. The second TPR peak (910 K) corresponds to the reduction of MoO3 to MoO2. At the third TPR peak (952 K), Mo4O11 was reduced to MoO2 and most of the β-FeMoO4 was transformed to Fe2Mo3O8 and Fe3O4. The Mössbauer spectrum of FeMo3O8 can be fitted with two doublets (IS = 0.90 mm/sec, QS = 0.58 mm/sec and IS = 1.03 mm/sec, QS = 1.05 mm/sec). It is interesting to note that at this stage some Fe2+ ions were reoxidized to Fe3+, and Fe3O4 is formed, probably due to the reaction between Mo6+ and Fe2+ in β-FeMoO4. At the fourth TPR peak (1014 K), β-FeMoO4 was completely converted and the Fe-Mo alloy (a singlet in the Mössbauer spectrum with IS = -0.21 mm/sec) was formed, resulting from the reduction of MoO2 and Fe3O4 or Fe2Mo3O8. At the last peak (1233 K), all the metal oxides (MoO2 and Fe3O4 or Fe2Mo3O8) were reduced to metals. The products detected are Fe3Mo alloy and metallic molybdenum.

A study on the reduction behavior of Fe2(MoO4)3 with a combined in-situ temperature-programmed reduction-M?ssbauer spectroscopic technique

The Reduction Behavior of Fe-Mo-O Catalysts Studied by Temperature-Programmed Reduction Combined with in Situ Mössbauer Spectroscopy and X-Ray Diffraction

The Reduction of Mg–Fe–O and Mg–Fe–Al–O Complex Oxides Studied by Temperature-Programmed Reduction Combined with in Situ Mössbauer Spectroscopy

A Study of In-Situ Mössbauer Spectroscopy on Fe−Mo Oxides for Selective Oxidation of Toluene

Reduction of Supported Iron Oxide Studied by Temperature-Programmed Reduction Combined with Mössbauer Spectroscopy and X-ray Diffraction

A study on the reduction behavior of silica supported iron and platinum-iron catalysts

Investigation on the reduction process of Fe-Ce oxides by TRP-in situ Mössbauer spectroscopy

Study on the Reduction Behavior of Zirconia Supported Iron Oxide Catalysts by Temperature-Programmed Reduction Combined within SituMössbauer Spectroscopy

STUDY ON THE REDUCIBILITY AND SURFACE STATE OF MoO 3 SUPPORTED ON THE SURFACE OF γ-AI 2 O 3 , TiO 2 AND SiO 2 BY XPS

Temperature-dependent Formation of Redox Sites in Molybdenum Trioxide Studied by Electron Paramagnetic Resonance Spectroscopy

A study on reduction behaviors of the supported platinum–iron catalysts

Studies of TPR in situ Fe-57 MBS on the reduction behavior of the gamma-Al2O3 supported iron and platinum-iron catalysts

Study on the Structure and Reduction Behaviour of the Iron–zirconium Oxide System

Investigation on the Kinetics and Mechanism of Aluminothermic Reduction of Molybdenum Trioxide: Non-isothermal Kinetics

In situ Mössbauer investigation of iron oxide catalyst in water gas shift reaction – Impact of oxyreduction potential and temperature

Exploring phase formation and magnetic transitions in Sm(Fe1−xMnx)14B by Mössbauer spectroscopy

Reduction Property of Rare Earth Oxide Doped Molybdenum Oxide

A Mössbauer Study of In–Fe2O3/HZSM-5 Catalysts for the Selective Catalytic Reduction of NO by Methane

Following the Structural Changes of Iron Oxides during Reduction under Transient Conditions

An investigation on aluminothermic reduction of MoO3 in domestic microwave oven

Temperature-programmed reduction and reduction kinetics of Mo-Ce oxides