Abstract:The reduction processes of Fe-Mo-O catalysts with different Fe/Mo atomic ratios were studied by means of temperature-programmed reduction (TPR). In particular, the reduction process of a sample with an Fe/Mo ratio of 0.29 was investigated in detail in combination with in situ Mössbauer spectroscopy (MBS) and X-ray diffraction (XRD). Five peaks are observed in the TPR profile of this sample with peak temperatures at 853, 910, 952, 1014, and 1233 K, respectively, indicating that the reduction of the catalyst proceeds via five stages. MBS and XRD showed that the phases in the sample are MoO3 and Fe2(MoO4)3 before TPR. At the first TPR peak (853 K), Fe2(MoO4)3 was completely transformed into β-FeMoO4 and Mo4O11, while MoO3 was not affected. The β-FeMoO4 phase that formed can convert to α-FeMoO4 when the reduced sample is exposed to air at room temperature. The second TPR peak (910 K) corresponds to the reduction of MoO3 to MoO2. At the third TPR peak (952 K), Mo4O11 was reduced to MoO2 and most of the β-FeMoO4 was transformed to Fe2Mo3O8 and Fe3O4. The Mössbauer spectrum of FeMo3O8 can be fitted with two doublets (IS = 0.90 mm/sec, QS = 0.58 mm/sec and IS = 1.03 mm/sec, QS = 1.05 mm/sec). It is interesting to note that at this stage some Fe2+ ions were reoxidized to Fe3+, and Fe3O4 is formed, probably due to the reaction between Mo6+ and Fe2+ in β-FeMoO4. At the fourth TPR peak (1014 K), β-FeMoO4 was completely converted and the Fe-Mo alloy (a singlet in the Mössbauer spectrum with IS = -0.21 mm/sec) was formed, resulting from the reduction of MoO2 and Fe3O4 or Fe2Mo3O8. At the last peak (1233 K), all the metal oxides (MoO2 and Fe3O4 or Fe2Mo3O8) were reduced to metals. The products detected are Fe3Mo alloy and metallic molybdenum.

A study on reduction behaviors of the supported platinum–iron catalysts

A study on the reduction behavior of silica supported iron and platinum-iron catalysts

Studies of TPR in situ Fe-57 MBS on the reduction behavior of the gamma-Al2O3 supported iron and platinum-iron catalysts

Reduction of Supported Iron Oxide Studied by Temperature-Programmed Reduction Combined with Mössbauer Spectroscopy and X-ray Diffraction

Study on the Reduction Behavior of Zirconia Supported Iron Oxide Catalysts by Temperature-Programmed Reduction Combined within SituMössbauer Spectroscopy

Isobutane dehydrogenation and Pt LIII-edge XAFS studies on γ-Al2O3 supported Pt-containing catalysts *

Pt L III -edge XANES and EXAFS studies on γ-Al 2 O 3 supported Pt catalysts

Pt Lm-edge xanes and exafs studies on γ-Al2O3 supported pt catalysts

The Reduction Behavior of Fe-Mo-O Catalysts Studied by Temperature-Programmed Reduction Combined with in Situ Mössbauer Spectroscopy and X-Ray Diffraction

The Reduction of Mg–Fe–O and Mg–Fe–Al–O Complex Oxides Studied by Temperature-Programmed Reduction Combined with in Situ Mössbauer Spectroscopy

Reductive Treatment of Pt Supported on Ti0.8Sn0.2O2-C Composite: A Route for Modulating the Sn-Pt Interactions

Study of Pt Dispersion on Ce Based Supports and the Influence on the CO Oxidation Reaction

Surface structure and reaction performances of highly dispersed and supported bimetallic catalysts

Surface structure and catalytic performance of supported PtSn catalysts

De-reducibility Mechanism of Titanium on Maghemite Catalysts for the SCR Reaction: an in Situ DRIFTS and Quantitative Kinetics Study

Dispersion and support dictated properties and activities of Pt/metal oxide catalysts in heterogeneous CO oxidation

A study on the reduction behavior of Fe2(MoO4)3 with a combined in-situ temperature-programmed reduction-M?ssbauer spectroscopic technique

Weak Affinity for CO of Platinum Group Metal Nanoparticles Supported on Partially Reduced Iron Oxides

Understanding the catalysis of noble metals in reduction of iron oxide by hydrogen: insights from DFT calculations

Strong Metal-Support Interaction and Catalytic Properties of Anatase and Rutile Supported Palladium Catalyst Pd/TiO2

Study of the Interfacial Structure of a Pt/α-Al2O3 Model Catalyst under High-Temperature Hydrogen Reduction