STUDY ON THE REDUCIBILITY AND SURFACE STATE OF MoO 3 SUPPORTED ON THE SURFACE OF γ-AI 2 O 3 , TiO 2 AND SiO 2 BY XPS

Gui Linlin,Zhong Bianxiao,Tang Youqi

DOI: https://doi.org/10.3866/PKU.WHXB19850503

1985-01-01

Acta Physico-Chimica Sinica

Abstract:MoO3/y-Al2O3, MoO3/TiO2, and MoO2/Sio(2) samples prepared by impregnation method were reduced at 480 degrees C by H-2 flow(atm, 50ml min(-1)) for an hour and characterized by XPS without exposure to the air. The ration of have been measured and compared with that of the oxidative precursors (Fig.1-3). For All samples which contain crystalline MoO3, the ratios are dramatically increased after reduction. We consider that a lot of molybdena has migrated from internal to external surface of the carriors during reduction. The monolayer molybdena supprted on gamma-Al2O3, TiO2 or SiO2 carriers shows quite different behaviours. On TiO2, it condensed slightly. On SiO2, it migrated partly from internal to external surface of the carrier. On gamma-Al2O3, it neither condensed nor migrated. It can be inferred that the order of interaction between molybdena and the surfaces of the carriers is : Mo(Al)> Mo >(Si). This is also the order of the stabilities ofthe monolayer of molybdena on these carriers. Computer fitting for Mo3d spectra shows that there are only Mo-v and Mo-IV in nearly all the reduced samples. As the fraction of Mo-IV increases with the content of MoO3 in reduced Mo(Al) and Mo(Si) samples, it indicates that the surfaces of these two carriers are heterogeneous. For reduced Mo(Ti) samples, there exists of turning point on the curve of Mo-IV fraction versus MoO3 contents (Fig.6). The content of MoO3 at this point agrees with the dispersed threshold value determined by XPS, XRD, and NH4OH extration((4)). Before it, the fraction of Mo-IV. the order of reducibilities of MoO3 for the three systems is : Mo(A)< Mo(Ti)< Mo(Si). It is probably subject to the interactions between molybdens and thhe carriers.