Abstract:In this paper, surface state and properties of MoO3 supported onto the surface of TiO2/gamma-Al2O3 carrier (i. e. TiO2 supported onto the gamma-Al2O3) are reported. Carrier we selected is S-20 of which TiO2 loading is 0.20g/g g-Al2O3. The physico-chemical propeties of the carrier was described in reference [6].MoO3 supported on carrier was prepared in two ways, one is general impregnation method and another is that the MoO3 and S-20 powders were mixed throughly and then the mixture was calcined at 450 degrees C for 24 hrs. The surface state of MoO2/TiO2/gamma-Al2O3 was characterized by using XRD, XPS, LRS and ammonia leaching techniques. It shows that the surface properties of it are quite different from MoO3 supporteed on TiO2 or gamma-Al2O3. This results are of benefit to developing new catalysts.The experimental results of XRD quantitative analysis and XPS intensity ratio and LRS quantitative analysis show that the utmost dispersion capacity of MoO3 on the surface of S-20 approaches 0.32g MoO3/g S-20 which is much bigger than the value calculated by close-packed model. However, the utmost monolayer dispersion capacity of MoO3 supported on TiO2 or gamma-Al2O3 meets the calculated value very well. It illustrates that the new carrier wo made has an ability to increasing the MoO3 dispersion capacity to 23% more.The results of LRS and ammonia leaching and XRD experimetns reveal the chemical state of MoO3 supported on S-20 carrier. When MoO3 loadining is less than 0.140/g S-20, a part of dispersed state MoO3 is dissolved into ammonia water and the ratio of dissolved part and undissolved part is 7:3. This is in line with the results of ammonia leaching of MoO3/TiO3 and MoO3/gamma-Al2O3 system. However, when MoO3 loading is bigger than 0.140g/S-20, the increment of MoO3 is dissolved into the ammona water completly. The results of LRS show that Mo species dissolved into ammonia water resides in octahedrally coordinated sites Mo(O) and Mo species undissolved resides in the tetrahedrally coordinated sites Mo(T). The results of LRS quantitative analysis shows that MoO3 surface species Mo*O) increases with the increase of MoO3 loading in the raange of lower MoO3 loading and MoO3 surface species Mo(O) is no longer increase with the increase of MoO3 loading when MoO3 loading is bigger that 0.25 g/g S-20. It follows that the increment of MoO3 in the range of 0,25-0.31g MoO3/g S-20 might be a new type of MoO3 species. Furthermore the LRS results indicate that in the range of 0.25-0.31 g MoO3/g S-20, the increment of MoO3 shows 1002cm(-1) Raman peak which some author assigned it to Al-2(MoO4)(3). In our case, we believe that it is small cluster of three dimensional polymolebdate because it also is dissolved into ammonia water. The distribution of the species of MoO3 supported onto the surface of S-20 carrier is described in the following figure.[GRAPHICS].

An XPS study of La2O3 and In2O3 influence on the physicochemical properties of MoO3/TiO2 catalysts

The Synergy Effect in Tio2 Supported Bi-Mo Catalysts for Facile and Environmentally-Friendly Synthesis of Pyridylaldehydes from Oxidation of Picolines

Influence of Titanium Oxide on the Surface Interactions of MO (m=cu and Ni)/γ-Al2O3 Catalysts

APPLICATION OF XPS TO STUDYING DISPERSION AND SURFACE STATE FOR MoO 3 SUPPORTED ON THE SURFACE OF TiO 2 , Γ-Al 2 O 3 AND SiO 2

Influence of the Host Oxide of Sulfated-Titania Catalysts on Partial Oxidation Methanol Reaction

MAS NMR, TPR, and TEM Studies of the Interaction of NiMo with Alumina and Silica–alumina Supports

Surface State and Properties of Moo3 Supported Onto the Surface of Tio2/Gamma-Al2o3 Carrier

Effects of MoO on Dispersion of Vanadia and Low-Temperature NH3-SCR Activity of Titania Supported Catalysts: Liquid Acidity and Steric Hindrance

STUDY ON THE REDUCIBILITY AND SURFACE STATE OF MoO 3 SUPPORTED ON THE SURFACE OF γ-AI 2 O 3 , TiO 2 AND SiO 2 BY XPS

Influence of texture structures of TiO2 supports on surface properties and SCR performance of V2 O5-MoO3/TiO2 catalyst

New Insight into the Support Effect on HDS Catalysts: Evidence for the Role of Mo-support Interaction on the MoS2 Slab Morphology

Studies on selective oxidation of methane to methanol over Mo/La-Co-O catalyst

Dispersion behaviors of molybdena on so4 2-modified TiO2 (rutile and/or anatase)

The Mo Loading Effect on Thermo Stability and SO2 Oxidation of SCR Catalyst

A Study of In-Situ Mössbauer Spectroscopy on Fe−Mo Oxides for Selective Oxidation of Toluene

Activities Of Mo(M=Cu And Ni)/Tio2/Gamma-Al2o3 Catalysts In Co Oxidation

XPS Characterization of Carbon Nanotube Supported CoMo Hydrodesulfurization Catalysts

Least squares curve fitting in Mo3d X-ray photoelectron spectra for determination of oxidation states of supported molybdenum catalysts.

Interactions of Molybdenum Oxide with Various Oxide Supports: Calcination of Mechanical Mixtures

Mechanistic Insight into the Modification of the Surface Stability of In2O3 Catalyst Through Metal Oxide Doping

Dispersion and support dictated properties and activities of Pt/metal oxide catalysts in heterogeneous CO oxidation