Abstract:Propose a rolling method to efficiently prepare fiber metal laminates. The surface of Al alloy sheets is treated with laser and coupling agent to achieve the purpose of toughening interface of composite laminates. In this study, a highly efficient method for preparing Al/CFRTP/Al composite laminates by roller preparation was proposed. Three different surface treatments, namely, anodic oxidation, laser texture and surface modification, were used to improve the strength of the metal‐fiber interface. Results show that composite laminates can be prepared efficiently by using reasonable roll pressing technology. The composite laminates with a thickness of 3 mm has good shear strength when the reduction amount is 0.02 mm. Laser texturing increases the contact area at the laminate interface. The surface roughness of Al alloy sheet is improved after laser texture. Moreover, the matrix in the fiber layer of the laminate can be embedded in the gullies formed by the laser texture to form a mechanical interlocking structure. The shear strength of the laminates was further increased when the laser scanning spacing was 2 mm. The highest shear strength of the laminate is 52.4 MPa after using a coupling agent to modify the surface of the Al alloy sheet. X‐ray photoelectron spectroscopy analysis showed that a new chemical bond was generated at the interface between CFRTP and the Al alloy sheet modified with silane coupling agent, thereby forming a molecular bridge among different materials. Mechanical interlocking structure and the generation of new chemical bonds cause the interface to need to absorb more energy during the failure process, which is conducive to the improvement of the interface strength. Highlights Propose roller pressing to prepare Al/CFRTP/Al composite laminates. Effect of laser texture of the laminates interface is clarified. Mechanism of coupling agents at the interface has been elucidated. Efficient preparation of thermoplastic fiber metal laminates has been achieved.

Interfacial Modification for an Aluminum/epoxy Resin Laminated Composite

Metal Surface Nanopatterning for Enhanced Interfacial Adhesion in Fiber Metal Laminates

Effect of Different Coupling Agents on Interfacial Properties of Fibre-Reinforced Aluminum Laminates

Surface Modification of Copper for Adhesion Promotion by Polybenzimidazole

On the interfacial adhesion of fiber metal laminates using surface modified aluminum 7475 alloy for aviation industries – a study

Interfacial Modification of Polymer/metal Joints by a Two-Component Coupling System of Polybenzimidazole and 2-Mercaptobenzimidazole

Experimental study of the interfacial micromechanics of multifunctional unidirectional carbon fiber reinforced polymer composite laminates with copper mesh

Interfacial Modification and Performance Enhancement of Carbon Matrix/aluminum Composites

Enhanced mechanical and dielectric properties of lamellar aluminum phosphate/bismaleimide composites by interface modification with maleimidopropyl triethoxysilane

Unravelling the Influence of Surface Modification on the Ultimate Performance of Carbon Fiber/Epoxy Composites

Interface evolution and strengthening of two-step roll bonded cu/Al clad composites

Rolling preparation process and interface toughening mechanism of Al/CFRTP/Al composite laminates

Effect of surface functional modification of nano-alumina particles on thermal and mechanical properties of epoxy nanocomposites

Forming Epoxy Coatings on Laser-Engraved Surface of Aluminum Alloy to Reinforce the Bonding Joint with a Carbon Fiber Composite

Enhancing the Mechanical properties of CF-Reinforced Epoxy Composites through Chemically Surface Modification of Carbon Fibers via Novel Two-Step Approach by Addition of Epichlorohydrin

Effect of Metal Surface Topography on the Interlaminar Shear and Tensile Strength of Aluminum/Polyamide 6 Polymer-Metal-Hybrids

Effect of Inorganic–organic Interface Adhesion on Mechanical Properties of Al2O3/polymer Laminate Composites

Effect of copper coating on interfacial properties, interfacial thermal resistance, microstructure evolution and mechanical properties of aluminum matrix composites

Reinforcement study of anodizing treatment with various temperatures on aluminum substrates for stronger adhesive bonding with carbon fiber composites

The effect of adhesive bonding between aluminum and composite prepreg on the mechanical properties of carbon-fiber-reinforced metal laminates

Effect of electrochemical anodic oxidation modification on the interfacial properties of carbon fiber reinforced polyimide composites