Abstract:The interface structure and infiltration effect between reinforcement (CFs) and Al matrix have a significant impact upon comprehensive properties of the resulting carbon-fibre-reinforced Al matrix (CF/Al) composites. In present study, Ni coatings with different thicknesses were evenly coated onto carbon fibres (CFs) via electroplating for the purpose of promote the interface combining effect and reduce adverse interfacial reaction betwixt CFs and Al matrix. The influence of pH value (2, 3, 4, 5, 6), current density (0.1 A, 0.2 A, 0.3 A, 0.4 A, 0.5 A, 0.6 A), electroplating time (2 min, 4 min, 6 min) on surface appearance and tensile strength of Ni-coated CFs were discussed. The results show that the Ni-coated CFs with excellent integrity and mechanical properties was obtained at a current density of 0.4 A and a pH of 5. Subsequently, twin-roll casting and T6 heat treatment process were used to fabricate CF/Al composites with varying Ni coating thicknesses. Using SEM, TEM and tensile property testing, the impact of Ni coating thickness (0 μm, 0.35 μm, 0.58 μm, 0.76 μm) on interfacial microstructures and mechanical characteristics of CF/Al composites were examined. The results exhibit that the 0.76 μm Ni-coated CF/Al composites exhibit best UTS and elongation of 151.6 MPa and 11.7 %, respectively. This is due to a thicker Ni coating preventing the CFs against reaction with Al matrix during processing the composites, which reduces the generation of Al 4 C 3 phase. However, when the coating thickness is 0.35 μm, adverse chemical interactions occur at interface of Al-CFs, leading to the formation of an Al 4 C 3 phase. Finally, the strengthening mechanism of Ni-coated CF/Al composites was analyzed, and its strengthening model was established. This study can provide a pratical route to prepare and applicate the high-quality continuous CF/Al composites.

Effect of copper coating on interfacial properties, interfacial thermal resistance, microstructure evolution and mechanical properties of aluminum matrix composites

Effect of Cu coating thickness on carbon fiber surface on microstructure and mechanical properties of carbon fiber reinforced aluminum matrix composites

Effect of interfacial stability on microstructure and properties of carbon fiber reinforced aluminum matrix composites

Study on Metallurgically Prepared Copper-Coated Carbon Fibers Reinforced Aluminum Matrix Composites

Effect of Cu/Ni Coating on the Interface and Mechanical Properties of Cf/2024Al Composites

Synergistic enhancing effect of tungsten-copper coated graphite flakes and aluminum nitride nanoparticles on microstructure, mechanical and thermal properties of copper matrix composites

Improvement of interfacial interaction and mechanical properties in aluminum matrix composites reinforced with Cu-coated carbon nanotubes

Effect of Cu/Ni coating on the interface and mechanical properties of C f /2024Al composites

Improved wettability and mechanical properties of metal coated carbon fiber-reinforced aluminum matrix composites by squeeze melt infiltration technique

The effect of nickel coating on the mechanical properties and failure modes of continuous carbon fiber reinforced aluminum matrix composites

Fabrication, Mechanical and Thermal Properties of Copper Coated Graphite Films Reinforced Copper Matrix Laminated Composites Via Ultrasonic-Assisted Electroless Plating and Vacuum Hot-Pressing Sintering

Effect of Alumina Coating and Extrusion Deformation on Microstructures and Thermal Properties of Short Carbon Fibre–al Composites

Formation and effect of intermetallic compounds in the interface of copper/aluminum composites under rolling conditions

Effect of annealing temperature on microstructure and tensile properties of copper/aluminum composite thin strip

The influence of interface products on the mechanical and electrical properties of graphene aluminum composites

Effect of copper coated graphite powder content on the microstructure and properties of Cu/C composite

Effect of Pure Cu Foil Interlayer on the Microstructure and Mechanical Behavior of Mg/Al Composite Sheet

Effects of the addition of CNTs and Al alloying on the microstructure and properties of Cu-(Al)/CNTs composites

Effect of surface modification on interfacial microstructures and mechanical properties of continuous CF/Al composites

Effect of Copper on Microstructure and Performance of WC/NiAl/TiC Composite Coatings by Laser Cladding

Effects of Cu Content on Microstructures and Compressive Mechanical Properties of CNTs/Al-Cu Composites