Experimental and Theoretical Investigation of Laser Pretreatment on Strengthening the Heterojunction Between Carbon Fiber Reinforced Plastic and Aluminum Alloy.
Yuyao Li,Shun Meng,Qianming Gong,Yilun Huang,Jianning Gan,Ming Zhao,Bin Liu,Lei Liu,Guisheng Zou,Daming Zhuang
DOI: https://doi.org/10.1021/acsami.9b04080
IF: 9.5
2019-01-01
ACS Applied Materials & Interfaces
Abstract:Besides aluminum alloy, lightweight carbon fiber reinforced plastics (CFRP) have been adopted progressively in automobiles in order to save energy and reduce emission, so constructing a reliable heterojunction between aluminum alloys and CFRP comes to be the key issue. In this study, ultra-fast picosecond infrared (IR) laser and excimer ultraviolet (UV) laser were introduced to pretreat the joint surface to enhance the adhesive strength. Scanning electron microscope, white light interferometry and X-ray photoelectron spectroscopy examinations indicated that, due to the energy absorptivity for the two lasers was different, the variation of the roughness, wettability and chemical composition were a little different for the patterned surface. Correspondingly, the shear strengths of the adhesive joints were increased from 5.6 MPa to 24.8 MPa and 21.9 MPa for IR and UV laser pretreated samples, respectively. Furthermore, finite element analysis was adopted to evaluate the effects of strengthened mechanical interlocking and fortified chemical bonding force on the enhancement of joint strength. It was shown that chemical bonding, instead of mechanical interlocking, played the dominant role in reinforcing the heterogeneous joints. As a whole, picosecond IR laser was more preferable for surface pretreatment in adhesive heterojunctions due to its higher processing and enhancing efficiency.