Investigation of laser-patterned biomimetic microstructures on CFRP and AA5052 surfaces to enhance their single-lap bonding strength

Shih-Feng Tseng,Yu-Sheng Chen,Tang-Wei Gao,Chil-Chyuan Kuo

DOI: https://doi.org/10.1016/j.compositesa.2023.107980

IF: 9.463

2023-12-29

Composites Part A Applied Science and Manufacturing

Abstract:This study focused on laser patterning of the biomimetic microstructures of gecko and tree frog patterns on the bonding surface of CFRP and AA5052 to improve their single-lap bonding strength. Laser-patterned biomimetic microstructures produced a rough surface and a superhydrophilic characteristic. A confocal laser microscope, contact angle measurement equipment and Fourier transform infrared spectroscopy were utilized to examine the surface roughness, wettability characteristic, and chemical bond of CFRP and AA5052, respectively. After the 8-week aging test, the lap shear strength of the test samples without pattern and with gecko and tree frog patterns was 2.22 ± 0.82 MPa, 9.26 ± 0.29 MPa, and 8.56 ± 0.15 MPa, respectively, which decreased approximately 75.8%, 10.96% and 13.09% compared to the unaging tests, respectively. The biomimetic microstructures of laser-ablated gecko patterns were helpful in enhancing the bonding strength of heterogeneous materials and in resisting drastic changes in the environment.

materials science, composites,engineering, manufacturing