Ferromagnetism and Double Magnetic Phase Transitions in Rapidly Solidified Mn1.13ni1.03fe0.23ge0.61 Ribbons

S. C. Ma,Y. Wu,Y. L. Huang,Y. Y. Gong,Y. H. Hou,J. F. Ou,Z. C. Zhong,D. H. Wang,Y. W. Du

DOI: https://doi.org/10.1016/j.jallcom.2013.11.063

IF: 6.2

2014-01-01

Journal of Alloys and Compounds

Abstract:The rapidly solidified Mn1.13Ni1.03Fe0.23Ge0.61 ribbons are prepared by the melt-spinning technique in argon atmosphere. A single phase with the Ni2In-type structure is confirmed by XRD means in the melt-spun ribbons at room temperature. What is more important, a ferromagnetic phase transition (around similar to 186 K) with a zero thermal hysteresis followed by another magnetic transition (around similar to 166 K) with a thermal hysteresis of similar to 2 K is achieved. Double magnetic transitions lead to two successive magnetic entropy peaks with the same sign accordingly. The origin of ferromagnetism and double magnetic phase transitions in melt-spun Mn1.13Ni1.03Fe0.23Ge0.61 ribbons is discussed. (C) 2013 Elsevier B. V. All rights reserved.