Structure And Exchange Bias Of Ni50mn37sn13 Ribbons

Yunbo Yang,Xiaobai Ma,Xuegang Chen,Jun Wei,Rui Wu,Jingzhi Han,Honglin Du,Cheng Wang,Shunquan Liu,Yingchang Yang,Yanwen Zhang,Jinbo Yang

DOI: https://doi.org/10.1063/1.3672244

IF: 2.877

2012-01-01

Journal of Applied Physics

Abstract:Ni50Mn37Sn13 ribbons were produced by the melt-spinning method. Structure and magnetic measurements on the Ni50Mn37Sn13 ribbons indicated that it is ferromagnetic below 340 K and undergoes an austenitic-to-martensitic phase transition just below room temperature. The austenitic phase has the cubic L2(1) structure, with the excess manganese atoms occupying the 4(b) sites. The martensitic phase has an orthorhombic structure. With increasing applied magnetic field, the martensite start temperature M-s and martensite finish temperature M-f shift to lower temperatures because of the field-induced phase transition. The exchange-bias effect is observed and strongly varied with different cooling fields at low temperature. At 5 K, the exchange-bias field reaches a maximum of 290 Oe when the cooling field increases to 200 Oe, and then reduces sluggishly with further increase of the cooling field because of weakening of exchange coupling between antiferromagnetic and ferromagnetic interfaces. (C) 2012 American Institute of Physics. [doi:10.1063/1.3672244]