Multiscale microstructural evolution of Fe–Ni–Al–Ti alloy with high magnetization
Si-Yi Chen,Ji-Bing Sun,Li-Zhu Wang,Hang-Qian Zhang,Xu-Ming Li,Chun-Xiang Cui
DOI: https://doi.org/10.1016/j.physb.2024.415825
IF: 2.988
2024-03-10
Physica B Condensed Matter
Abstract:The Fe–15Ni–3Al–1Ti ribbons are produced by melt-spinning the annealed ingots at 10–40 m/s. The annealed ingots consist of Fe 3 Ni grains and α-Fe-type grain boundary phase, forming a columnar grain microstructure in the vertical direction and getting the maximum saturation magnetic polarization ( J s ) of 1.88 ± 0.03 T in the cross-section. Before and after the annealing, the ribbons form a cellular structure composed of the Fe 3 Ni intragranular phase and γ-(Fe, M), Fe 7 Ni 3 , or α-(Fe, M) cell boundary phases. Formation of enhanced orientation is the primary mechanism for obtaining a high J s of 2.35 ± 0.07 T in the ribbons. The grain and grain boundary size of the ribbons is reduced by the phase transformation induced by annealing at 600 °C. The phase transformation processes of the ribbons before and after annealing are as follows: L→γ→melt−spunFe3Ni+γ1→annealedFe3Ni+Fe7Ni3 when melt-spinning at a speed of 10–25 m/s, and L→γ→melt−spunFe3Ni+Fe7Ni3→annealedFe3Ni+α−(Fe,Ni) at 40 m/s. Finally, the multiscale microstructure evolution models are used to summarize the phase transformation process of the alloys.
physics, condensed matter